A wide series of copolymer materials with various contents of 4-vinyl-diisopropyl-phtalate ester (10–90 mol%), divinylbenzene (1–11 mol%) and styrene, as monomers, were obtained by radical copolymerization. In the last steps of the synthesis, diisopropyl ester functionalities were converted into the form of N-hydroxyphthalimide (NHPI) rings. The obtained materials with the NHPI groups immobilized in the copolymer structure were studied by various physicochemical techniques, including FT-IR, UV-Vis-DR, XPS, elemental analysis, and tested as catalysts in aerobic oxidation of p-methoxytoluene in the presence of Co(II) acetate co-catalyst. Conversion of the aromatic substrate was correlated with the NHPI content and cross-linking degree. The best catalytic performance (conversions higher than 23%) was achieved for the copolymer catalysts containing 60% and 30% of 4-vinyl-diisopropyl-phtalate ester. At too high concentrations of NHPI and DVB, some of the NHPI groups were transformed into inactive (C=O)-N=O species or not available due to embedding inside the copolymer structure. The mechanism of the process involving both NHPI centers, forming phthalimide N-oxyl (PINO) radicals, and Co(II) cations was discussed. Stability of the developed catalysts was also tested. The opening of imide rings took place during the catalytic process, resulting in the formation of carboxyl groups and the release of hydroxylamine molecules. The deactivated catalyst could be easily regenerated by repeating two last steps of closing imide ring.

The polycondensation of resorcinol and formaldehyde in a water–ethanol mixture using the adapted Stöber method was used to obtain resol resins. An optimization of synthesis conditions and the use of an appropriate stabilizer (e.g., poly(vinyl alcohol)) resulted in spherical grains. The resins were carbonized in the temperature range of 600–1050 °C and then chemically activated in an aqueous HNO₃ solution, gaseous ammonia, or by an oxidation–reduction cycle (soaking in a HNO₃ solution followed by treatment with NH₃). The obtained carbons were characterized by XRD, the low-temperature adsorption of nitrogen, SEM, TGA, and XPS in order to determine degree of graphitization, porosity, shape and size of particles, and surface composition, respectively. Finally, the materials were tested in phenol adsorption. The pseudo-second order model perfectly described the adsorption kinetics. A clear correlation between the micropore volume and the adsorption capacity was found. The content of graphite domains also had a positive effect on the adsorption properties. On the other hand, the presence of heteroatoms, especially oxygen groups, resulted in the clogging of the pores and a decrease in the amount of adsorbed phenol.

The paper discusses a formation of Mt–PAA composite containing a natural montmorillonite structure partially exfoliated by poly(acrylic acid) introduced through intercalation polymerization of acrylic acid. Mt–PAA was subsequently modified by controlled adsorption of Co²⁺ ions. The presence of aluminosilicate packets (clay) and carboxyl groups (hydrogel) led to the deposition of significant amounts of Co²⁺ ions, which after calcination formed the Co₃O₄ spinel particles. The conditions of the Co²⁺ ions’ deposition (pH, volume and concentration of Co(NO₃)₂ solution, as well as a type of pH-controlling agent) were widely varied. Physicochemical characterization of the prepared materials (including X-ray fluorescence (XRF), X-ray powder diffraction (XRD), low-temperature nitrogen adsorption, X-ray photoelectron spectroscopy (XPS) and temperature-programmed reduction (H₂-TPR)) revealed that the modification conditions strongly influenced the content as well as the distribution of the Co₃O₄ active phase, tuning its reducibility. The latter parameter was, in turn, very important from the point of view of catalytic activity in the combustion of aromatic volatile organic compounds (VOCs) following the Mars–van Krevelen mechanism.