In this study, a Pt/anodized aluminum oxide (AAO) catalyst was prepared by the anodization of an Al alloy (Al6082, 97.5% Al), followed by the incorporation of Pt via an incipient wet impregnation method. Then, the Pt/AAO catalyst was evaluated for autocatalytic hydrogen recombination. The Pt/AAO catalyst’s morphological characteristics were determined by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The average Pt particle size was determined to be 3.0 ± 0.6 nm. This Pt/AAO catalyst was tested for the combustion of lean hydrogen (0.5–4 vol% H₂ in the air) in a recombiner section testing station. The thermal distribution throughout the catalytic surface was investigated at 3 vol% hydrogen (H₂) using an infrared camera. The Al/AAO system had a high thermal conductivity, which prevents the formation of hotspots (areas where localized surface temperature is higher than an average temperature across the entire catalyst surface). In turn, the Pt stability was enhanced during catalytic hydrogen combustion (CHC). A temperature gradient over 70 mm of the Pt/AAO catalyst was 23 °C and 42 °C for catalysts with uniform and nonuniform (worst-case scenario) Pt distributions. The commercial computational fluid dynamics (CFD) code STAR-CCM+ was used to compare the experimentally observed and numerically simulated thermal distribution of the Pt/AAO catalyst. The effect of the initial H₂ volume fraction on the combustion temperature and conversion of H₂ was investigated. The activation energy for CHC on the Pt/AAO catalyst was 19.2 kJ/mol. Prolonged CHC was performed to assess the durability (reactive metal stability and catalytic activity) of the Pt/AAO catalyst. A stable combustion temperature of 162.8 ± 8.0 °C was maintained over 530 h of CHC. To confirm that Pt aggregation was avoided, the Pt particle size and distribution were determined by TEM before and after prolonged CHC.

Dibenzyltoluene/perhydro-dibenzyltoluene (H₀DBT/H₁₈DBT) is considered a promising liquid organic hydrogen carrier (LOHC) pair for the storage and transportation of green hydrogen (H₂). However, at the point of use, the catalytic dehydrogenation of H₁₈DBT is still limited by mass transport limitations. To address this issue, the dehydrogenation of H₁₈DBT was successfully conducted on Pt/Al₂O₃-coated foams in both an unstirred tank reactor and a fixed-bed reactor (FBR). A performance comparison between coated foams and pellets in the tank reactor revealed that H₂ productivities were 12–59% higher in the foam-based reactor than in the pellet-based reactor. Since the textural properties of the foam-supported and pellet-based catalysts were similar, the higher degree of dehydrogenation (DoD) and H₂ productivity achieved by the former were attributed to the geometric properties of the foam structure. Long-term tests performed in the FBR demonstrated the ability of the coated foams to maintain steady activity for >16 h on stream. However, the single-pass DoDs achieved were 34–38%. By recycling the partially dehydrogenated products three times into the FBR, the DoD improved to 63%. The results of this study demonstrated the capabilities of the coated foams in the process intensification of LOHC dehydrogenation reactors.