Bone ash waste can be used to fabricate clay ceramic bricks, consequently managing their pollution of the environment. This is because bone ash (BA) and clay predominantly consist of calcium and alumina-silicate, respectively, which are components of clay ceramic brick (CCB) materials. This study aims to investigate the effect of bone ash and temperature on the physio-chemical and mechanical properties of CCB. Different percentages of bone ash (5%, 10%, 15%, and 20%) were added to clay and heat treated at temperatures of 100 °C, 300 °C, 600 °C, and 900 °C, and their compressive strengths were measured. Prior to the determination of their mechanical properties, the CCB chemical and phase compositions were characterized using FTIR spectroscopy and X-ray diffraction (XRD). The CCB microstructure was evaluated with scanning electron microscopy (SEM) and the compressive strength was tested. The results suggest that the addition of bone ash (10% and 15%) improves the compressive strength and water absorption properties after heat treatment of CCB at higher temperatures.

The quantity of polymer waste in our communities is increasing significantly. It is therefore necessary to consider reuse or recycling waste to avoid an increase in the risk to public health. This project is aimed at using pulverized low-density polyethylene (LDPE) waste as a source to reinforce and improve compressive strength, and to reduce the water absorption of geopolymer ceramics (GC). Clay:LDPE composition consisting of 5%, 10%, and 15% LDPE was geopolymerized with an NaOH/Na₂SiO₃ solution and cured at 30 °C and 50 °C. Characterization of the geopolymer samples was carried out using XRF and XRD. The microstructure was analyzed by SEM and chemical bonding by FTIR. The SEM micrographs showed LDPE particle pull-out on the geopolymer ceramics’ fracture surface. The result showed that the compressive strength increases with the addition of pulverized polymer waste compared to the controlled without LDPE addition. Water absorption decreased with an increase in LDPE addition in the geopolymer ceramics composite.