In this study, the effects of dissolved-gas concentration in liquid water on the nucleation and growth of bubbles and nanobubble (NB) generation were investigated by measuring the concentration and size distribution of NBs. Three types of liquids with different dissolved-gas concentrations—undersaturated, saturated, and supersaturated deionized (DI) water—were prepared, and NBs were generated via ultrasonic irradiation. As the dissolved-gas concentration increased, a large number of bubbles with relatively large diameters (several tens of micrometers or more) were generated, but the NB concentration decreased. The surface tension decreased with an increase in the dissolved gas concentration, and thus, the tensile strength which required for bubble growth became lower. Therefore, there were barely any NBs in supersaturated conditions because of the accelerated nucleation and bubble growth.

In this study, highly concentrated hydrogen nanobubble water was utilized as the blending water for cement mortar to improve its compressive and flexural strengths. Highly concentrated nanobubbles can be obtained through osmosis. This concentration was maintained by sustaining the osmotic time. The mortar specimens were cured for 28 days, in which the nanobubble concentration was increased. This improved their flexural strength by 2.25–13.48% and compressive strength by 6.41–11.22%, as compared to those afforded by plain water. The nanobubbles were densified at high concentrations, which caused a decrease in their diameter. This increased the probability of collisions with the cement particles and accelerated the hydration and pozzolanic reactions, which facilitated an increase in the strength of cement. Thermogravimetric analysis and scanning electron microscopy were used to confirm the development of calcium silicate hydrate (C-S-H) and hydration products with an increase in the nanobubble concentration. Quantitative analysis of the hydration products and the degree of hydration were calculated by mineralogical analysis.

In recent years, minuscule gas bubbles called bulk nanobubbles (BNBs) have drawn increasing attention due to their unique properties and broad applicability in various technological fields, such as biomedical engineering, water treatment, and nanomaterials. However, questions remain regarding the stability and behavior of BNBs. In the present work, BNBs were generated in water using a gas–liquid mixing method. NB analysis was performed using a nanoparticle tracking analysis (NTA) method to investigate the coarsening behavior of BNBs in water over time. The diameters of the BNBs increased, and their cubic radii increased linearly (r³ ~ t) over time. While the concentration of BNBs decreased, the total volume of BNBs remained the same. The size distribution of the BNBs broadened, and the concentration of larger BNBs increased over time. These results indicate that relatively small BNBs disappeared due to dissolution and larger BNBs grew through mass transfer between BNBs instead of coalescence. In other words, BNBs underwent Ostwald ripening: gas molecules from smaller BNBs diffused through the continuous phase to be absorbed into larger BNBs.

This study analyzed the effects of applying highly concentrated hydrogen nanobubble water (HNBW) on the workability, durability, watertightness, and microstructure of cement mixtures. The number of hydrogen nanobubbles was concentrated twofold to a more stable state using osmosis. The compressive strength of the cement mortar for each curing day was improved by about 3.7–15.79%, compared to the specimen that used general water, when two concentrations of HNBW were used as the mixing water. The results of mercury intrusion porosimetry and a scanning electron microscope analysis of the cement paste showed that the pore volume of the specimen decreased by about 4.38–10.26%, thereby improving the watertightness when high-concentration HNBW was used. The improvement in strength and watertightness is a result of the reduction of the microbubbles’ particle size, and the increase in the zeta potential and surface tension, which activated the hydration reaction of the cement and accelerated the pozzolanic reaction.