A nano-structured Co oxide electrode (with a Ni substrate) was successfully prepared using an entirely electrochemical process, which included the co-deposition of a Ni-Cu alloy film, selective etching of Cu from the film, and anodic deposition of Co oxide on the obtained nano-porous Ni substrate which had an average pore size of approximately 100 nm and a pore density of about 10(13) m(-2). The excellent electrochemical activity of the prepared electrode was demonstrated in terms of its pseudocapacitive performance, which was evaluated using cyclic voltammetry (CV) in 1 M KOH solution. The specific capacitance of the nano-structured Co oxide measured at a potential scan rate of 10 mV s(-1) was as high as 2200 F g(-1), which is over ten times higher than that of a flat oxide electrode (209 F g(-1)). The highly porous Co oxide also had superior kinetic performance as compared to a flat electrode. At a high CV scan rate of 50 mV s(-1), the two electrodes retained 94% and 59%, respectively, of their specific capacitances measured at 5 mV s(-1).

To achieve high energy and power densities, we developed a high-voltage 2.5 V electrochemical pseudo-capacitor with a maximum energy density of 304 W h kg⁻¹ based on MnO₂ nanowires electrodeposited on nickel foam as electrode with a novel Li-ion quasi-ionic liquid as electrolyte.

With a simple electrochemical process, we prepared nano-architectured CuO electrodes with a 3D hierarchically porous structure and an excellent supercapacitive performance. These nano-architectured CuO electrodes were processed through co-deposition of a Ni–Cu layer on Ni foam, selective etching of Cu from the Ni–Cu film (leaving tentacle-like nanoporous Ni), and anodic deposition of CuO nanoribbons (NRs) on the tentacle-like nanoporous Ni/Ni foam substrate. Because of its unique nano-architecture, the prepared CuO nanoribbon-on-Ni-nanoporous/Ni foam (CNRNP) electrode shows exceptional performance of energy storage relative to a conventional version of the electrode. The CNRNP electrode has also a superior kinetic performance relative to CuO nanoflake-on-Ni foam (CNFNF) and flake-like CuO (FLC) electrodes. Besides its excellent cyclic stability, an exceptionally large specific capacitance of 880 and 800 F g⁻¹ (deducting the substrate capacitance from the total) for the CNRNP electrode is obtained at scan rates of 10 and 200 mV s⁻¹, respectively. The excellent pseudocapacitive characteristics of CNRNP electrodes associated with the variation of the Cu oxidation state during charge and discharge cycles were elucidated with in situ X-ray absorption near-edge structure (XANES) spectra.