Through its dependence on low symmetry crystal phases, ferroelectricity is inherently a property tied to the lower temperature ranges of the phase diagram for a given material. This paper presents conclusive evidence that in the case of ferroelectric Al_1−xSc_xN, low temperature has to be seen as a purely relative term, since its ferroelectric-to-paraelectric transition temperature is confirmed to surpass 1100 °C and thus the transition temperature of virtually any other thin film ferroelectric. We arrived at this conclusion through investigating the structural stability of 0.4–2 μm thick Al_0.73Sc_0.27N films grown on Mo bottom electrodes via in situ high-temperature x-ray diffraction and permittivity measurements. Our studies reveal that the wurtzite-type structure of Al_0.73Sc_0.27N is conserved during the entire 1100 °C annealing cycle, apparent through a constant c/a lattice parameter ratio. In situ permittivity measurements performed up to 1000 °C strongly support this conclusion and include what could be the onset of a diverging permittivity only at the very upper end of the measurement interval. Our in situ measurements are well-supported by ex situ (scanning) transmission electron microscopy and polarization and capacity hysteresis measurements. These results confirm the structural stability on the sub-μm scale next to the stability of the inscribed polarization during the complete 1100 °C annealing treatment. Thus, Al_1−xSc_xN, there is the first readily available thin film ferroelectric with a temperature stability that surpasses virtually all thermal budgets occurring in microtechnology, be it during fabrication or the lifetime of a device—even in harshest environments.

Analog switching in ferroelectric devices promises neuromorphic computing with the highest energy efficiency if limited device scalability can be overcome. To contribute to a solution, one reports on the ferroelectric switching characteristics of sub‐5 nm thin Al_0.74Sc_0.26N films grown on Pt/Ti/SiO₂/Si and epitaxial Pt/GaN/sapphire templates by sputter‐deposition. In this context, the study focuses on the following major achievements compared to previously available wurtzite‐type ferroelectrics: 1) Record low switching voltages down to 1 V are achieved, which is in a range that can be supplied by standard on‐chip voltage sources. 2) Compared to the previously investigated deposition of ultrathin Al_1−xSc_xN films on epitaxial templates, a significantly larger coercive field (E_c) to breakdown field ratio is observed for Al_0.74Sc_0.26N films grown on silicon substrates, the technologically most relevant substrate‐type. 3) The formation of true ferroelectric domains in wurtzite‐type materials is for the first time demonstrated on the atomic scale by scanning transmission electron microscopy (STEM) investigations of a sub‐5 nm thin partially switched film. The direct observation of inversion domain boundaries (IDB) within single nm‐sized grains supports the theory of a gradual domain‐wall driven switching process in wurtzite‐type ferroelectrics. Ultimately, this should enable the analog switching necessary for mimicking neuromorphic concepts also in highly scaled devices.