The 3D-printed bioactive ceramic incorporated Poly(ε-caprolactone) (PCL) scaffolds show great promise as synthetic bone graft substitutes. However, 3D-printed scaffolds still lack adequate surface properties for cells to be attached to them. In this study, we modified the surface characteristics of 3D-printed poly(ε-caprolactone)/hydroxyapatite scaffolds using O2 plasma and sodium hydroxide. The surface property of the alkaline hydrolyzed and O2 plasma-treated PCL/HA scaffolds were evaluated using field-emission scanning microscopy (FE-SEM), Alizarin Red S (ARS) staining, and water contact angle analysis, respectively. The in vitro behavior of the scaffolds was investigated using human dental pulp-derived stem cells (hDPSCs). Cell proliferation of hDPSCs on the scaffolds was evaluated via immunocytochemistry (ICC) and water-soluble tetrazolium salt (WST-1) assay. Osteogenic differentiation of hDPSCs on the scaffolds was further investigated using ARS staining and Western blot analysis. The result of this study shows that alkaline treatment is beneficial for exposing hydroxyapatite particles embedded in the scaffolds compared to O2 plasma treatment, which promotes cell proliferation and differentiation of hDPSCs.

Post-surgery failure of dental implants due to alveolar bone loss is currently critical, disturbing the quality of life of senior dental patients. To overcome this problem, bioceramic or bone graft material is loaded into the defect. However, connective tissue invasion instead of osteogenic tissue limits bone tissue regeneration. The guided bone regeneration concept was adapted to solve this problem and still has room for improvements, such as biochemical similarity or oriented structure. In this article, an aligned electrospun-guided bone regeneration barrier with xenograft equine bone-derived nano hydroxyapatite (EBNH-RB) was fabricated by electrospinning EBNH/PCL solution on high-speed rotating drum collector and fiber characterization, viability and differentiation enhancing properties of mesenchymal dental pulp stem cell on the barrier was determined. EBNH-RB showed biochemical and structural similarity to natural bone tissue electron microscopy image analysis and x-ray diffractometer analysis, and had a significantly better effect in promoting osteogenesis based on the increased bioceramic content by promoting cell viability, calcium deposition and osteogenic marker expression, suggesting that they can be successfully applied to regenerate alveolar bone as a guided bone regeneration barrier.

Cryopreservation, the most common method of preserving stem cells, requires post-processing because it produces trauma to the cells. Post-thawing trauma typically induces cell death, elevates reactive oxygen species (ROS) concentration, and lowers mitochondrial membrane potential (MMP). Although this trauma has been solved using antioxidants, we attempted to use photobiomodulation (PBM) instead of chemical treatment. We used a 950-nm near-infrared LED to create a PBM device and chose a pulsed-wave mode of 30 Hz and a 30% duty cycle. Near-infrared radiation (NIR) at 950 nm was effective in reducing cell death caused by hydrogen peroxide induced-oxidative stress. Cryodamage also leads to apoptosis of cells, which can be avoided by irradiation at 950 nm NIR. Irradiation as post-processing for cryopreservation had an antioxidant effect that reduced both cellular and mitochondrial ROS. It also increased mitochondrial mass and activated mitochondrial activity, resulting in increased MMP, ATP generation, and increased cytochrome c oxidase activity. In addition, NIR increased alkaline phosphatase (ALP) activity, a biomarker of differentiation. As a result, we identified that 950 nm NIR PBM solves cryodamage in human stem cells from the apical papilla, indicating its potential as an alternative to antioxidants for treatment of post-thawing trauma, and further estimated its mechanism.

The regulation of apoptosis is the primary goal of ablation therapy. Irreversible electroporation (IRE) is a promising non-thermal tissue ablation-based therapy that induces apoptosis by manipulating electrical conditions. This study aimed to investigate IRE-induced gastric tissue apoptosis in response to changes in the electric field intensity, followed by the repair process. Among the 52 rats used in this study, 24 were used to explore apoptosis, and 28 were used to study regeneration. The apoptosis-to-necrosis ratio of the electrical field strength was evaluated using terminal deoxynucleotidyl transferase-mediated deoxyuridine triphosphate nick-end labeling and caspase-3 immunohistochemistry. The size of IRE-induced ulcers in the gastric tissue continuously increased with increasing electrical intensity (r² = 0.830, p < 0.001). The level of apoptosis gradually decreased after peaking at 200 V (1000 V/cm). The size of the 400 V-ablated ulcers continued to decrease, and they were not visible by day 14. The proliferation and migration of epithelial cells with fibroblasts were observed on day 3 and augmented on day 7 post-ablation. This investigation demonstrated the biphasic activation of apoptosis with respect to the electrical field strength. Visually and histologically, IRE-induced gastric ulcers demonstrated complete tissue regeneration after two weeks.

Background/Aims: Irreversible electroporation (IRE) is a relatively new ablation method. However, the application of IRE ablation in the treatment of biliary disease has not been attempted. A minimally invasive approach using endoscopic retrograde cholangiopancreatography (ERCP) can be a novel therapeutic modality for IRE ablation. In this study, we aimed to investigate the feasibility of endoscopic IRE for the biliary tract using an animal model. Methods: A new catheter-type electrode was developed for endoscopic IRE ablation of the biliary tract. We performed ERCP and endoscopic IRE ablations in the normal common bile duct of Yorkshire pigs. The experimental setting of IRE was 500 V/cm (50 pulses, 100-mu s length). The animals were sacrificed after 24 hr, and the ablated bile duct was examined. Results: Well-demarcated focal color changes were observed on the mucosa of the common bile duct. The depth of change after IRE was confined to the mucosal and submucosal layers. Apoptotic changes in the bile duct were observed only around the IRE ablation area. Immunohistochemistry assay showed cell death in the bile duct along the electrode. Conclusions: Endoscopic IRE ablation using ERCP was successfully performed in the common bile duct. It can be a potential option for the treatment of biliary tumors.

Conventional irreversible electroporation (IRE) with low-frequency pulsed electric field (LF-PEF) is used to induce cell death; however, it has several disadvantages including a long procedure time and severe muscle contraction due to high-voltage electric field. This study investigates a novel IRE protocol with high-frequency pulsed electric field (HF-PEF) of 500 Hz repetition to ablate the prostate tissue in beagles for treatment of prostate cancer. A finite element analysis was performed to validate optimal electrical field strength for the procedure. In total, 12 beagles received HF-PEF of 500 Hz and were sacrificed at 4 h, 4 days, and 28 days (3 each). The remaining three beagles underwent sham procedure. The outcomes of HF-PEF were assessed by histological responses. HF-PEF successfully decellularized the prostate tissues 4 h after the treatment. The prostate glands, duct, and urethra were well preserved after IRE with HF-PEF. The ablated prostatic tissues were gradually regenerated and appeared similar to the original tissues 28 d after IRE with HF-PEF. Moreover, electrocardiography and hematology demonstrated that IRE with HF-PEF did not seriously affect the cardiac tissue. HF-PEF was effective and safe in the beagle prostate and effectively induced the ablation and gradually recovered with cellular regeneration.