We present new data about the chemical and structural characteristics of bauxite residue (BR) from Greek Al industry, using a combination of microscopic, analytical, and spectroscopic techniques. SEM-EDS indicated a homogeneous dominant “Al-Fe-Ca-Ti-Si-Na-Cr matrix”, appearing at the microscale. The bulk chemical analyses showed considerable levels of Th (111 μg g⁻¹), along with minor U (15 μg g⁻¹), which are responsible for radioactivity (355 and 133 Bq kg⁻¹ for ²³²Th and ²³⁸U, respectively) with a total dose rate of 295 nGy h⁻¹. Leaching experiments, in conjunction with SF-ICP-MS, using Mediterranean seawater from Greece, indicated significant release of V, depending on S/L ratio, and negligible release of Th at least after 12 months leaching. STEM-EDS/EELS & HR-STEM-HAADF study of the leached BR at the nanoscale revealed that the significant immobility of Th⁴⁺ is due to its incorporation into an insoluble perovskite-type phase with major composition of Ca_0.8Na_0.2TiO₃ and crystallites observed in nanoscale. The Th L_III-edge EXAFS spectra demonstrated that Th⁴⁺ ions, which are hosted in this novel nano-perovskite of BR, occupy Ca²⁺ sites, rather than Ti⁴⁺ sites. That is most likely the reason of no Th release in Mediterranean seawater.

In this work, an examination of mining wastes of an albite deposit in south Spain was carried out using X-ray Fluorescence (XRF), X-ray diffraction (XRD), particle size analysis, thermo-dilatometry and Differential Thermal Analysis (DTA) and Thermogravimetric (TG) analysis, followed by the determination of the main ceramic properties. The albite content in two selected samples was high (65–40 wt. %), accompanied by quartz (25–40 wt. %) and other minor minerals identified by XRD, mainly kaolinite, in agreement with the high content of silica and alumina determined by XRF. The content of Na₂O was in the range 5.44–3.09 wt. %, being associated with albite. The iron content was very low (<0.75 wt. %). The kaolinite content in the waste was estimated from ~8 to 32 wt. %. The particle size analysis indicated values of 11–31 wt. % of particles <63 µm. The ceramic properties of fired samples (1000–1350 °C) showed progressive shrinkage by the thermal effect, with water absorption and open porosity almost at zero at 1200–1250 °C. At 1200 °C, the bulk density reached a maximum value of 2.38 g/cm³. An abrupt change in the phase evolution by XRD was found from 1150 to 1200 °C, with the disappearance of albite by melting in accordance with the predictions of the phase diagram SiO₂-Al₂O₃-Na₂O and the system albite-quartz. These fired materials contained as main crystalline phases quartz and mullite. Quartz was present in the raw samples and mullite was formed by decomposition of kaolinite. The observation of mullite forming needle-shape crystals was revealed by Scanning Electron Microscopy (SEM). The formation of fully densified and vitrified mullite materials by firing treatments was demonstrated.

Climate change has already had observable effects due to greenhouse gases (GHG) produced by human activities. Over the years, this becomes more evident as the concentration of GHG released in the atmosphere is concerningly increased as does the earth’s average temperature too. Hence, all countries and many independent organizations are taking actions to reduce the Global Warming phenomenon by setting targets for carbon dioxide emissions. The energy sector is proved to play the most important role in emissions reduction. Greece’s target for this sector is very ambitious in total transformation of energy mixture in the forthcoming years. Universities are also contributing to GHG emissions through their operations and members’ activities. Energy management at the University of Patras in Greece has already started since 2019 by installing energy meters going from manual calculations to an online system. The reliable records and accurate calculations proved as a very important action and a starting point for performing detailed analysis. In this study, there was an effort to calculate the CO₂ emissions of the University of Patras using the Carbon Campus Calculator. The results showed that the students commuting is the main source of GHG emissions at the University of Patras and the purchased electricity comes next. These two factors together comprise 60.2% of the total emissions and priority should be given to reducing their footprint. Specific targets were set up for 2030 in compliance with the National Plan for Energy and Climate of Greece. Moreover, an Action Plan managing carbon and energy more efficiently and creating a strong environmental culture among the community is proposed. In the future, the university’s management team should act proactively in every change at Patras University. An assessment on the environmental impact should take place before any decision making. If necessary, extra actions should be defined in order not to deviate from the targets and new standards set.

Portland cement is the most common type of cement and one of the most important ingredients in concrete. Concrete, on the other hand, is the most used building material worldwide just behind the water with an increasing usage trend in infrastructure for the upcoming years. During the production process of cement, massive CO₂ emissions are released into the environment, while large amounts of raw materials and energy are consumed. In the present study, Portland type cement was prepared in laboratory-scale by Greek Wet Fly Ash and Mill Scales, as well as conventional raw materials such as limestone, shale and lava. The experiments were conducted at 1450 °C and 1340 °C. The fired compositions were characterized by XRD, Q–XRD, optical microscopy, SEM/EDS and the concrete specimens were tested for their compressive strength. The results indicated that formation of cement clinker at lower temperatures (1340 °C) is feasible with the combined use of natural raw materials and industrial byproducts following the standard production route of cement industries. Finally, the so-obtained cement presented compressive strength values comparable to the conventional ones fired at 1450 °C.

The biggest challenge for our society, in order to foster the sustainable circular economy, is the efficient recycling of wastes from industrial, commercial, domestic and other streams. The transition to a circular economy is the goal of the European Commission’s Circular Economy Action, which was first launched in 2015. In 2020 the above action plan announced initiatives along the entire life cycle of the product, with the aim to make sustainable products the norm in the EU. Therefore, it is anticipated that the above action will result in an increase in Europe’s economic competitiveness, sustainability, resource efficiency and resource security. Within this context, the suitability of ferroalumina as a raw material in the blast furnace is investigated. Ferroalumina is the product of the high-pressure filter press dewatering process of the Greek red mud generated during the production of alumina by means of the Bayer cycle. Ferroalumina is a low-cost raw material and its possible charging in the blast furnace and/or steelmaking aggregates is a step towards industrial symbiosis, where the wastes, namely by-products, of an industry or an industrial process, become the raw materials for another. In the present work the effect of ferroalumina addition as a raw material was examined by smelting ferroalumina, blast furnace-slag, lime and scrap at 1550°C in a graphite crucible and a constant slag basicity. The increase of the alumina content in the slag improves the desulfurization capacity. Moreover, the silicon exchange between slag and metal was examined. The results indicate that the alkalis’ capacity of the slag increases with the addition of ferroalumina. The analysis of the finally obtained slag suggests that it could be suitable for utilization in slag-cement production.