In the current study, polymer nanocomposites (NCPs) based on poly (vinyl alcohol) (PVA) with altered refractive index and absorption edge were synthesized by means of a solution cast technique. The characterization techniques of UV–Vis spectroscopy and XRD were used to inspect the structural and optical properties of the prepared films. The XRD patterns of the doped samples have shown clear amendments in the structural properties of the PVA host polymer. Various optical parameters were studied to get more insights about the influence of CeO₂ on optical properties of PVA. On the insertion of CeO₂ nanoparticles (NPs) into the PVA matrix, the absorption edge was found to move to reduced photon energy sides. It was concluded that the CeO₂ nanoparticles can be used to tune the refractive index (n) of the host polymer, and it reached up to 1.93 for 7 wt.% of CeO₂ content. A detailed study of the bandgap (BG) was conducted using two approaches. The outcomes have confirmed the impact of the nanofiller on the BG reduction of the host polymer. The results of the optical BG study highlighted that it is crucial to address the ε” parameter during the BG analysis, and it is considered as a useful tool to specify the type of electronic transitions. Finally, the dispersion region of n is conferred in terms of the Wemple–DiDomenico single oscillator model.

Proton conducting nanocomposite solid polymer electrolytes (NSPEs) based on polyvinyl alcohol/ammonium nitrate (PVA/NH₄NO₃) and different contents of zinc oxide nanoparticles (ZnO-NPs) have been prepared using the casting solution method. The XRD analysis revealed that the sample with 2 wt.% ZnO-NPs has a high amorphous content. The ionic conductivity analysis for the prepared membranes has been carried out over a wide range of frequencies at varying temperatures. Impedance analysis shows that sample with 2 wt.% ZnO-NPs has a smaller bulk resistance compared to that of undoped polymer electrolyte. A small amount of ZnO-NPs was found to enhance the proton-conduction significantly; the highest obtainable room-temperature ionic conductivity was 4.71 × 10⁻⁴ S/cm. The effect of ZnO-NP content on the transport parameters of the prepared proton-conducting NSPEs was investigated using the Rice–Roth model; the results reveal that the increase in ionic conductivity is due to an increment in the number of proton ions and their mobility.