A solution processable, molecular organic semiconductor, 6,13-bis(triisopropylsilylethynyl) pentacene (TIPS-pentacene), was employed as hole transport material (HTM) in mesoscopic methylammonium lead iodide perovskite solar cells. TIPS-pentacene is potentially cost effective, exhibits a relatively high hole mobility and has a favourable HOMO level with respect to the valence band of perovskite. The photovoltaic performance of perovskite solar cells with TIPS-pentacene as HTM in its pristine form and with a dopant/additive was investigated and compared with classical spiro-OMeTAD based devices. Through solvoneering (solvent engineering) and concentration optimization TIPS-pentacene in its pristine form gave a very competitive power conversion efficiency (PCE) of 11.8% under 1 sun conditions. The open circuit voltage of 0.92 V and a short circuit current density of 20.86 mA cm⁻² for the devices with pristine TIPS-pentacene were higher compared to doped spiro-OMeTAD based devices under similar conditions, thus paving the use of TIPS-pentacene as an alternative to an expensive spiro-OMeTAD for large area integration in perovskite based solar cells.

Organic–inorganic hybrid perovskite solar cells have emerged as cost effective efficient light-to-electricity conversion devices. Unravelling the time scale and the mechanisms that govern the charge carrier dynamics is of paramount importance for a clear understanding and further optimization of the perovskite based devices. For the classical FTO/bulk titania blocking layer/mesoporous titania/perovskite/Spiro-OMeTAD (FTO/TPS) cell, further detailed and systematic studies of the ultrafast events related to exciton generation, electron and hole transfer, ultrafast relaxation are still needed. We characterize the initial ultrafast processes attributed to the exciton–perovskite lattice interactions influenced by charge transfer to the electron and hole transporters that precede the exciton diffusion into free charge carriers occurring in the sensitizer. Time-resolved transient absorption studies of the FTO/perovskite and FTO/TPS samples under excitation at different wavelengths and at low fluence 2 (μJ cm⁻²) indicate the sub-picosecond electron and hole injection into titania and Spiro-OMeTAD, respectively. Furthermore, the power-dependent femtosecond transient absorption measurements support the ultrafast charge transfer and show strong Auger-type multiparticle interactions at early times. We reveal that the decays of the internal trap states are the same for both films, while those at surfaces differ. The contribution of the former in the recombination is small, thus increasing the survival probability of the charges in the excited perovskite.

A low temperature (60 °C) encapsulation process based on a single thin (16 nm) coating of Al ₂ O ₃ prepared by atomic layer deposition.

A non-aggregated Zn(II)octa(2,6-diphenylphenoxy) phthalocyanine (coded as TT80) has been used as a hole-transporting material for perovskite solar cells. The cells were fabricated under three different configurations by changing the uptake solvent (chlorobenzene or toluene) and incorporating additives (bis(trifluoromethane) sulfonimide lithium salt (LiTFSI) and 4-tert-butylpyridine (TBP). A power conversion efficiency of 6.7% (AM1.5G standard conditions) was achieved for the best cell under optimized configuration.