One-step TiO2 nanoparticle synthesis based on the interaction between thiourea and metatitanic acid is applied for sulfur and carbon anatase codoping. The synthesis of the doped TiO2 has been monitored by means of differential thermal analysis and thermogravimetric analysis (DTA-TG), which allows determining the optimal thermal conditions for the process. Electron microscopy showed micrometer-sized (5–15 μm) randomly distributed crystal aggregates, consisting of many 15–40-nm TiO2 nanoparticles. The obtained phase composition and chemical states of the doping elements are analyzed by means of X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), infrared (IR) and Raman spectroscopies, and electron paramagnetic resonance (EPR). XRD displays in both samples (doped and pristine) the existence of only one crystalline phase—the tetragonal modification of TiO2—anatase. Further data assessment by means of Rietveld refinement allowed detection of a slight c lattice parameter and volume increase related to incorporation of the doping elements. XPS demonstrated the presence of carbon and sulfur as doping elements in the material. It was confirmed that carbon is in elemental form and also present in oxygen-containing compounds, which are adsorbed on the particle surface. The binding energy for sulfur electron core shell corresponds to the established data for sulfate compounds, where sulfur is in 6+ oxidation state. The synthesized S- and C-codoped TiO2 showed excellent photocatalytic performance during the degradation of organic dyes (rhodamine B, methylene blue), gas-phase oxidation of ethanol under visible light, and photocatalytic hydrogen generation from ethanol under ultraviolet light.

Photocatalytic degradation is a promising method for removing persistent organic pollutants from water because of its low cost (see solar-driven photocatalysis), high mineralisation of pollutants, and low environmental impact. Photocatalysts based on transition metal dichalcogenides (TMDs) have recently attracting high scientific interest due to their unique electrical, mechanical, and optical properties. A MoS₂ photocatalyst of the layered structure was managed to photodegrade methylene blue (MB) under visible light irradiation. The catalyst was thoroughly characterised using SEM, AFM, powder XRD, UV–Vis, Raman, and XPS measurements. The photocatalytic degradation of the MB solution was conducted under the following conditions: (i) reductive and (ii) oxidative. The impact of optical and electronic properties, and the MoS₂-MB interaction on photocatalytic activity, was discussed. The apparent rate constants (k_app) of degradation were 3.7 × 10^–3; 7.7 × 10^–3; 81.7 × 10^–3 min⁻¹ for photolysis, oxidative photocatalysis, and reductive photocatalysis. Comparison of the degradation efficiency of MB in reductive and oxidative processes indicates the important role of the reaction with the surface electron. In the oxidation process, oxygen reacts with an electron to form a superoxide anion radical involved in further transformations of the dye, whereas, in the reduction process, the addition of an electron destabilises the chromophore ring and leads to its rupture.

In the present study, diamond-like carbon films with embedded Ag nanoparticles (DLC:Ag) were deposited by reactive magnetron sputtering. Structure of the films was investigated by Raman scattering spectroscopy. Atomic force microscopy was used to define thickness of DLC:Ag films as well as to study the surface morphology and size distribution of Ag nanoparticles. Optical absorbance and reflectance spectra of the films were studied in the 180–1100-nm range. Air annealing effects on structure and optical properties of the DLC:Ag were investigated. Annealing temperatures were varied in the 180–400 °C range. Changes of size and shape of the Ag nanoclusters took place due to agglomeration. It was found that air annealing of DLC:Ag films can result in graphitization following destruction of the DLC matrix. Additional activation of surface-enhanced Raman scattering (SERS) effect in DLC:Ag films can be achieved by properly selecting annealing conditions. Annealing resulted in blueshift as well as significant narrowing of the plasmonic absorbance and reflectance peaks. Moreover, quadrupole surface plasmon resonance peaks appeared. Modeling of absorption spectra of the nanoclusters depending on the shape and surrounding media has been carried out.

The paper presents experimental studies of dielectric properties of nanofluids based on ethylene glycol and SC-TiO2 nanoparticles with average size of 15–40 nm with various mass concentrations. The dielectric permittivity both real part and imaginary part as a function of temperature and frequency were measured. Also, dependence ac conductivity on frequency, temperature, and mass concentration were investigated. Based on the curves of ac conductivity, dc conductivity was calculated, and 400 % enhancement in dc conductivity was exposed.