In this article, we present the results of the research into the characteristics of the conditions of heating and explosive destruction of Al-Cu, Fe-Ti, Fe-Cu, and Fe-Pb wires under a pulse of current with the density of 10⁷ A/cm². It has been shown that the energy that is deposited into the wire may depend on the relation between the thermophysical parameters and specific electric resistivity of the metals. It has been determined that under a pulse of current, the wires may explode synchronously or non-synchronously. During a synchronous explosion of wires, a single voltage pulse is generated. In the case of non-synchronous explosion, the wires explode in a succession, thus generating two voltage pulses. We suggested a dimensionless parameter that allows for predicting whether an electrical explosion of two wires of dissimilar metals is synchronous or non-synchronous. According to the research findings, non-synchronous nature of wire explosion may impact the formation of bimetallic particles through the explosion of two intertwined wires made of dissimilar metals.

We have prepared a composite thin coating by incorporation of CuFe₂O₄/Cu₂O/CuO nanoparticles in polymethyl methacrylate (PMMA) matrix by using the solution casting method. The electrical explosion of two twisted wires (EETW) was used to obtain multicomponent CuFe₂O₄/Cu₂O/CuO nanoparticles with an average particle size of 20–70 nm. The microscopic studies showed that the nanoparticles in the composite coatings are evenly distributed. However, nanoparticles are strongly agglomerated as the powder concentration in the coating increases to 5 wt.% and 10 wt.%, as the size of particle agglomerates increases to 50 and 100 μm, respectively. Therefore, nanoparticles were pre-treated with ultrasound when introduced into the PMMA matrix. The thermal stability of the composite coating does not change with the introduction of CuFe₂O₄/Cu₂O/CuO nanoparticles in the amount of 5 wt.%. The inclusion of nanoparticles in the PMMA matrix significantly enhances its antibacterial activity. The addition of 5 wt.% nanoparticles inhibited the growth of E. coli by 100% and the growth of MRSA by 99.94% compared to pure PMMA already after 3 h of exposure of bacteria on the surface of the composites. This research provides an easy-to-manufacture and cost-efficient method for producing a CuFe₂O₄/Cu₂O/CuO/PMMA composite coating with a broad application as an antibacterial material.

Electrical explosion of aluminum wires has been shown to be a versatile method for the preparation of bimodal nano/micro powders. The energy input into the wire has been found to determine the relative content of fine and coarse particles in bimodal aluminum powders. The use of aluminum bimodal powders has been shown to be promising for the development of high flowability feedstocks for metal injection molding and material extrusion additive manufacturing.

Polymethylmethacrylate (PMMA) is the most commonly used bone void filler in orthopedic surgery. However, the biocompatibility and radiopacity of PMMA are insufficient for such applications. In addition to insufficient biocompatibility, the microbial infection of medical implants is one of the frequent causes of failure in bone reconstruction. In the present work, the preparation of a novel PMMA-based hydroxyapatite/ZnFe₂O₄/ZnO composite with heterophase ZnFe₂O₄/ZnO NPs as an antimicrobial agent was described. ZnFe₂O₄/ZnO nanoparticles were produced using the electrical explosion of zinc and iron twisted wires in an oxygen-containing atmosphere. This simple, highly productive, and inexpensive nanoparticle fabrication approach could be readily adapted to different applications. From the findings, the presented composite material showed significant antibacterial activity (more than 99% reduction) against P. aeruginosa, S. aureus, and MRSA, and 100% antifungal activity against C. albicans, as a result of the combined use of both ZnO and ZnFe₂O₄. The composite showed excellent biocompatibility against the sensitive fibroblast cell line 3T3. The more-than-70% cell viability was observed after 1–3 days incubation of the sample. The developed composite material could be a potential material for the fabrication of 3D-printed implants.

The reactivity of passivated aluminum nanopowders was studied. Organic coating has been shown to enhance the resistance of aluminum nanopartic1es to the effect of water vapor and causes changes in the parameters of the nonisothermal oxidation by air oxygen. Passivation of aluminum nanopowders has been established to increase the temperature of oxidation onset and the heat release rate.

The paper studies a bimodal metal powder composition designed to prepare feedstock for powder injection molding, as well as microstructure and porosity of sintered pats. Two kinds of metal powder compositions are used, in particular, a mixture of micro- and nanopowders and a bimodal powder prepared with dispersion of steel wire. The feedstock is prepared by mixing a bimodal metal powder composition with acetylacetone and paraffin wax. The microstructure of the debound parts is observed by scanning electron microscopy. The sintered parts are characterized by density measurements and metallographic analysis. The technique of the metal powder composition proves to affect the characteristics of sintered parts. Nanoparticles are shown in the interstitial spaces among the microparticles upon mixing micro- and nanopowders, but the regular distribution of nanoparticles on the surface of microparticles is observed in the bimodal powder providing the reduction of the porosity of sintered parts and increasing the density to the proper density of steel.