Background: Ethylene and vinyl acetate (EVA) and polyether block amide (PEBA) are recently the most widely used materials for advanced footwear technology (AFT) that has been shown to improve running economy (RE). This study investigated the effects of these midsole materials on RE and biomechanics, in both fresh and worn state (after 450 km).Methods: Twenty‐two male trained runners participated in this study. Subjects ran four 4‐min trials at 13 km‧h⁻¹ with both fresh EVA and PEBA AFT and with the same models with 450 km of wear using a randomized crossover experimental design. We measured energy cost of running (W/kg), spatiotemporal, and neuromuscular parameters.Results: There were significant differences in RE between conditions (p = 0.01; n² = 0.17).There was a significant increase in energy cost in the worn PEBA condition compared with new (15.21 ± 1.01 and 14.87 ± 0.99 W/kg; p < 0.05; ES = 0.54), without differences between worn EVA (15.13 ± 1.14 W/kg; p > 0.05), and new EVA (15.15 ± 1.13 w/kg; ES = 0.02). The increase in energy cost between new and worn was significantly higher for the PEBA shoes (0.32 ± 0.38 W/kg) but without significant increase for the EVA shoes (0.06 ± 0.58 W/kg) (p < 0.01; ES = 0.51) with changes in step frequency and step length. The new PEBA shoes had lower energy cost than the new EVA shoes (p < 0.05; ES = 0.27) with significant differences between conditions in contact time.Conclusion: There is a clear RE advantage of incorporating PEBA versus EVA in an AFT when the models are new. However, after 450 km of use, the PEBA and EVA shoes had similar RE.

Material Extrusion Additive Manufacturing (MEAM) is a novel technology to produce polymeric, metallic, and ceramic complex components. Filaments composed of a high-volume content of metal powder and a suitable binder system are needed to obtain metallic parts. Thermal and energetic controversies do not affect MEAM technology, although common in other additive manufacturing (AM) techniques. High thermal conductivity and reflectivity of copper to high-energy beams are the most challenging properties. A material extrusion technique to produce high density and quality copper parts is deeply studied in this research. Characterization of the filament, printed parts, brown parts and final sintered parts is provided. The sintering stage is evaluated through density analysis of the sintered copper parts, as well as their dimensional accuracy after part shrinkage inherent to the sintering process. The mechanical behavior of sintered parts is assessed through tensile, hardness and impact toughness tests. In addition, the measured electrical and thermal conductivities are compared to those obtained by other AM technologies. High-density components, with 95% of relative density, were successfully manufactured using MEAM technology. Similar or even superior mechanical, thermal and electrical properties than those achieved by other 3D printing processes such as Electron Beam Melting, Selective Laser Melting and Binder Jetting were obtained.