This paper presents a comprehensive review of recent advancements in surface engineering of metals, encompassing techniques, characterization methods and applications. The study emphasizes the significance of surface engineering in enhancing the performance and functionality of metallic materials in various industries. The paper discusses the different techniques employed in surface engineering, including physical techniques such as thermal spray coatings and chemical techniques such as electroplating. It also explores characterization methods used to assess the microstructural, topographical, and mechanical properties of engineered surfaces. Furthermore, the paper highlights recent advancements in the field, focusing on nanostructured coatings, surface modification for corrosion protection, biomedical applications, and energy-related surface functionalization. It discusses the improved mechanical and tribological properties of nanostructured coatings, as well as the development of corrosion-resistant coatings and bioactive surface treatments for medical implants. The applications of surface engineering in industries such as aerospace, automotive, electronics, and healthcare are presented, showcasing the use of surface engineering techniques to enhance components, provide wear resistance, and improve corrosion protection. The paper concludes by discussing the challenges and future directions in surface engineering, highlighting the need for further research and development to address limitations and exploit emerging trends. The findings of this review contribute to advancing the understanding of surface engineering and its applications in various sectors, paving the way for future innovations and advancements.

An investigation of mechanical properties of Ti6Al4V produced by additive manufacturing (AM) in the as-printed condition have been conducted and compared with wrought alloys. The AM samples were built by Selective Laser Melting (SLM) and Electron Beam Melting (EBM) in 0°, 45° and 90°—relative to horizontal direction. Similarly, the wrought samples were also cut and tested in the same directions relative to the plate rolling direction. The microstructures of the samples were significantly different on all samples. α′ martensite was observed on the SLM, acicular α on EBM and combination of both on the wrought alloy. EBM samples had higher surface roughness (Ra) compared with both SLM and wrought alloy. SLM samples were comparatively harder than wrought alloy and EBM. Tensile strength of the wrought alloy was higher in all directions except for 45°, where SLM samples showed higher strength than both EBM and wrought alloy on that direction. The ductility of the wrought alloy was consistently higher than both SLM and EBM indicated by clear necking feature on the wrought alloy samples. Dimples were observed on all fracture surfaces.

Selective laser melting has a great potential to manufacture biocompatible metal alloy scaffolds or implants with a regulated porosity structure. This study uses five face-centered cubic (FCC) lattice structures, including FCC, FCC-Z, S-FCC, S-FCC-Z, and FCC-XYZ. Specimens with different lattice structures are fabricated using two laser energy densities, 71 J/mm³ and 125 J/mm³. Density, tensile, compressive and flexural test results exhibit the effect of laser parameters and lattice structure geometries on mechanical properties. The higher laser energy density of 125 J/mm³ results in higher properties such as density, strength, and Young’s modulus than the laser energy density of 71 J/mm³. The S-FCC lattice has the lowest density among all lattices. The mechanical tests result show specimen with FCC-XYZ lattice structures fabricated using a laser energy density of 125 J/mm³ meet the tensile properties requirement for human ribs. This structure also meets the requirement in flexural strength performance, but its stiffness is over that of human ribs. The compression test results of lattices are still incomparable due to unavailable compression data of the human ribs. In short, The FCC-XYZ lattice design fabricated by the 125 J/mm³ laser energy density parameter can be used to manufacture customized rib implants.

This review paper provides a comprehensive overview of the phenomenon of superlubricity, its associated material characteristics, and its potential applications. Superlubricity, the state of near-zero friction between two surfaces, presents significant potential for enhancing the efficiency of mechanical systems, thus attracting significant attention in both academic and industrial realms. We explore the atomic/molecular structures that enable this characteristic and discuss notable superlubric materials, including graphite, diamond-like carbon, and advanced engineering composites. The review further elaborates on the methods of achieving superlubricity at both nanoscale and macroscale levels, highlighting the influence of environmental conditions. We also discuss superlubricity’s applications, ranging from mechanical systems to energy conservation and biomedical applications. Despite the promising potential, the realization of superlubricity is laden with challenges. We address these technical difficulties, specifically those related to achieving and maintaining superlubricity, and the issues encountered in scaling up for industrial applications. The paper also underscores the sustainability concerns associated with superlubricity and proposes potential solutions. We conclude with a discussion of the possible future research directions and the impact of technological innovations in this field. This review thus provides a valuable resource for researchers and industry professionals engaged in the development and application of superlubric materials.

Inconel 718 (IN 718) powder is used for a laser powder bed fusion (LPBF) printer, but the mechanical properties of the as-built object are not suited to cold deep drawing applications. This study uses the Taguchi method to design experimental groups to determine the effect of various factors on the mechanical properties of as-built objects produced using an LPBF printer. The optimal printing parameters are defined using the result for the factor response to produce an as-built object with the greatest ultimate tensile strength (UTS), and this is used to produce a specimen for post-processing, including heat treatment (HT) and surface finishing. The HT parameter value that gives the maximum UTS is the optimal HT parameter. The optimal printing and HT parameter values are used to manufacture a die and a punch to verify the suitability of the manufactured tool for deep drawing applications. The experimental results show that the greatest UTS is 1091.33 MPa. The optimal printing parameters include a laser power of 190 W, a scanning speed of 600 mm/s, a hatch space of 0.105 mm and a layer thickness of 40 μm, which give a UTS of 1122.88 MPa. The UTS for the post-processed specimen increases to 1511.9 MPa. The optimal parameter values for HT are heating to 720 °C and maintaining this temperature for 8 h, decreasing the temperature to 620 °C and maintaining this temperature for 8 h, and cooling to room temperature in the furnace. Surface finishing increases the hardness to HRC 55. Tools, including a punch and a die, are manufactured using these optimized parameter values. The deep drawing experiment demonstrates that the manufactured tools that are produced using these values form a round cup of Aluminum alloy 6061. The parameter values that are defined can be used to manufacture IN 718 tools with a UTS of more than 1500 MPa and a hardness of more than 50 HRC, so these tools are suited to cold deep drawing specifications.

Selective laser melting technology is one of the metal additive manufacturing technologies that can convert metal powder to complex parts without the assembly process. This study aims to optimize the volumetric laser energy density for printing 3D metal objects with hinges geometry. The material is stainless steel 316L powder. The volumetric laser energy densities ranging from 4.1 J/mm³ to 119.1 J/mm³ are applied to fabricate 3D free-assembled hinges with various clearances of 0.38 mm, 0.39 mm, 0.40 mm, and 0.41 mm and investigate the relationship between volumetric laser energy density and clearance. A multibody model, consisting of nine segments with eight hinges, is proposed to be printed with the optimized volumetric laser energy density. The optical microscope and the hardness test are performed to observe the porosity and hardness property of the SLMed object. The result shows that laser energy densities between 105.5 J/mm³ and 119.1 J/mm³ can produce the high densification of SLMed objects with a porosity defect of 0.24% to 0.20% and hardness in the range of 207 HV to 215 HV. The optimization of laser energy densities is in the range of 105.5 J/mm³ to 119.1 J/mm³, which can be used to fabricate the movable hinges with a minimum clearance size of 0.41 mm. The proposed dinosaur object is printed successfully and all joints are rotatable.