Hydrogen evolution reaction (HER) was investigated on reduced graphene oxide (rGO)-supported Au and PdAu nanoparticles in acid solution. The graphene spread over glassy carbon (rGO/GC) was used as a support for the spontaneous deposition of Au and Pd. The resulting Au/rGO and PdAu/rGO electrodes were characterized using atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS) techniques. Phase AFM images have shown that the edges of the rGO sheets were active sites for the deposition of both Au and Pd. XPS analysis revealed that the atomic percentages of both Au and PdAu nanoparticles were slightly higher than 1%. The activity of the PdAu/rGO electrode for the HER was remarkably high, with the overpotential close to zero. HER activity was stable over a 3 h testing time, with a low Tafel slope of approx. −46 mV/dec achieved after prolonged hydrogen evolution at a constant potential.

PdPt bimetallic nanoparticles on carbon-based supports functioning as advanced electrode materials have attracted attention due to their low content of noble metals and high catalytic activity for fuel cell reactions. Glassy carbon (GC)-supported Pt and PdPt nanoparticles, as promising catalysts for the oxygen reduction reaction (ORR), were prepared by the electrochemical deposition of Pt and the subsequent spontaneous deposition of Pd. The obtained electrodes were examined using X-ray Photoelectron Spectroscopy (XPS), Atomic Force Microscopy (AFM), and electroanalytical techniques. An XPS analysis of the PdPt/GC with the highest ORR performance revealed that the stoichiometric ratio of Pd: Pt was 1:2, and that both Pt and Pd were partially oxidized. AFM images of PdPt₂/GC showed the full coverage of GC with PdPt nanoparticles with sizes from 100–300 nm. The ORR activity of PdPt₂/GC in an acid solution approached that of polycrystalline Pt (E_1/2 = 0.825 V vs. RHE), while exceeding it in an alkaline solution (E_1/2 = 0.841 V vs. RHE). The origin of the improved ORR on PdPt₂/GC in an alkaline solution is ascribed to the presence of a higher amount of adsorbed OH species originating from both PtOH and PdOH that facilitated the 4e-reaction pathway.

This study examines the kinetics and mechanism of the oxygen reduction reaction (ORR) on a polycrystalline rhodium electrode (Rh(poly)) in acidic and alkaline media, using rotating disc electrode measurements. This study found that the ORR activity of the Rh(poly) electrode decreases in the order of 0.1 M NaOH > 0.1 M HClO₄ > 0.05 M H₂SO₄ concerning the half-wave potentials. The Tafel slopes for ORR on Rh(poly) in the cathodic direction are 60 and 120 mV dec⁻¹ at low and high overpotentials, respectively, in perchloric acid and alkaline solutions. However, strongly adsorbed sulfate anions hinder the ORR on Rh(poly) in sulfuric acid, leading to higher Tafel slopes. The highest ORR activity of Rh(poly) in an alkaline media suggests the promoting role of the specifically adsorbed OH⁻ anions and RhOH. In all cases, ORR on Rh(poly) proceeds through the 4e-series reaction pathway.

The cobalt crystalline islands (Co_cryst) were electrochemically deposited onto a glassy carbon (GC) support and then modified by a facile spontaneous deposition of platinum. The electrocatalytic activity of the resulting Co_cryst-Pt core-shell catalyst was evaluated for the oxygen reduction reaction (ORR) in an alkaline medium. The XRD characterization of the Co_cryst-Pt islands revealed that the cobalt core had a hexagonal close-packed (hcp) crystalline structure, and that the platinum shell exhibited a crystalline structure with a preferential (111) orientation. SEM images showed that the average lateral size of the Co_cryst islands was 1.17 μm, which increased to 1.32 μm after adding platinum. The XPS analysis indicated that the outer layer of the bulk metallic Co_cryst islands was fully oxidized. During the spontaneous deposition of platinum, the outer Co(OH)₂ layer was dissolved, leaving the cobalt core in a metallic state, while the platinum shell remained only partially oxidized. The high electrochemically active surface area of the Co_cryst-Pt/GC electrode, along with a suitable crystalline structure of the Co_cryst-Pt islands, contributes to enhancing its ORR activity by providing a greater number of surface active sites for oxygen adsorption and subsequent reduction. The ORR on the Co_cryst-Pt catalyst occurs via a four-electron reaction pathway, with onset and half-wave potentials of 1.07 V and 0.87 V, respectively, which exceed those of polycrystalline platinum and a commercial benchmark Pt/C.