Mesoporous bioactive glass (MBG) is an extensively studied biomaterial used for the healing of bone defects. Its biological applications can be tailored by introducing metallic ions, such as strontium (Sr) and copper (Cu), which can enhance its functionalities, including osteogenetic, angiogenetic and antibacterial functionalities. In this study, Cu and Sr ions were co-doped (ratio 1:1) with x = 0.5, 1 and 2 mol% each in glass with an intended nominal composition of 80SiO₂-(15-2x)CaO-5P₂O₅-xCuO-xSrO and synthesized with an evaporation-induced self-assembly (EISA)-based sol-gel technique. XRD confirmed the amorphous nature of the glass, while compositional analysis using ICP-OES confirmed the presence of dopant ions with the required amounts. A TEM study of the MBG powders showed fringes that corresponded to the formation of a highly ordered mesoporous structure. The Cu-Sr-doped MBG showed a positive effect on apatite formation when immersed in SBF, although the release of Cu and Sr ions was relatively slow for 1 mol% of each co-dopant, which signified a stable network structure in the glass. The impact of the Cu and Sr ions on the osteoblast-like cell line MG-63 was assessed. At the particle concentrations of 1 wt./vol.% or lower, the cell viability was above 50%. An antibacterial test was conducted against Gram-negative E. coli and Gram-positive S. aureus bacteria. With a sequential increase in the co-doped ion content in the glass, the zone of inhibition for bacteria increased. The results suggest that the doping of MBG with Cu and Sr ions at up to 2 mol% can result in tailored sustained release of ions to enhance the applicability of the studied glass as a functional biomaterial for bone regeneration applications.

The addition of SiC or TiC nanoparticles to polycrystalline alumina matrix has long been known as an efficient way of improving the mechanical properties of alumina-based ceramics, especially strength, creep, and wear resistance. Recently, new types of nano-additives, such as carbon nanotubes (CNT), carbon nanofibers (CNF), and graphene sheets have been studied in order not only to improve the mechanical properties, but also to prepare materials with added functionalities, such as thermal and electrical conductivity. This paper provides a concise review of several types of alumina-based nanocomposites, evaluating the efficiency of various preparation methods and additives in terms of their influence on the properties of composites.

Vascularization is necessary in tissue engineering to keep adequate blood supply in order to maintain the survival and growth of new tissue. The synergy of biologically active ions with multi-target activity may lead to superior angiogenesis promotion in comparison to single-target approaches but it has been rarely investigated. In this study, polycaprolactone (PCL) fiber mats embedded with B and Co co-doped bioactive glass nanoparticles (BCo.BGNs) were fabricated as a tissue regeneration scaffold designed for promoting angiogenesis. BCo.NBGs were successfully prepared with well-defined spherical shape using a sol-gel method. The PCL fiber mats embedding co-doped bioactive glass nanoparticles were fabricated by electrospinning using benign solvents. The Young’s moduli of the nanoparticle containing PCL fiber mats were similar to those of the neat fiber mats and suitable for scaffolds utilized in soft tissue repair approaches. The mats also showed non-cytotoxicity to ST-2 cells. PCL fiber mats containing BCo.BGNs with a relatively high content of B and Co promoted the secretion of vascular endothelial growth factor to a greater extent than PCL fiber mats with a relatively low B and Co contents, which demonstrates the potential of dual ion release (B and Co) from bioactive glasses to enhance angiogenesis in soft tissue engineering.

Composite fibrous membranes based on poly(ɛ‐caprolactone) (PCL) and mesoporous bioactive glass nanoparticles (MBGNs) were fabricated by electrospinning. MBGNs and Zn‐doped MBGNs prepared by microemulsion sol–gel method were successfully incorporated inside the polymeric fibers of 240 and 385 nm in diameter for undoped and Zn‐doped PCL_MBGNs fibers, respectively. Thermal analysis showed that the concentration of MBGNs reached a maximum of around 21 wt% for Zn‐doped MBGNs. Both PCL_MBGNs and PCL_MBGNs_Zn composite membrane exhibited bioactivity after immersion in simulated body fluid (SBF). X‐ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) showed the evolution of composite membranes, confirming the formation of hydroxyapatite (HAp). However, the degradation products of membranes did not affect the viability and proliferation of murine stromal cells (ST‐2) and thus the new fiber structures represent a suitable environment for cell adhesion. Therefore, the incorporation of mesoporous glass nanoparticles doped with therapeutically active Zn ²⁺ ions inside the PCL fibers offers the possibility to create a multifunctional biomaterial suitable for drug delivery and tissue engineering.

This manuscript presents a systematic and detailed study of ion release from 45S5 bioactive glass to develop a methodology to directly monitor dissolved ions in a simulated fluid via inductively coupled plasma optical emission spectrometry (ICP OES). For the kinetic study, two dynamic tests, an inline ICP test and a flow-through test, are performed with the same flow rate, temperature, pH, ionic strength of the solution, and sample surface to leaching solution volume ratio. The flow-through test allows for the measurement of an initial dissolution rate, as well the maximum amount of any species released from the surface of the glass. In addition, the data from the inline ICP test are obtained by immediate and direct monitoring of ions from the first minutes of contact of the glass with aqueous fluids with pH values of 4 and 7.4. The overall dissolution rates of the tested commercial bioactive glass in simulated body fluid (SBF) (pH 7.4) were significantly lower compared to the initial rate acquired. The methodology developed in this study can be applied to monitor the controlled release of ions with additional therapeutic functionalities, where the amount of ions released in the first minutes can be critical for the resulting biological performance.