We here describe a rapid method for synthesizing hollow core, porous crystalline calcium carbonate microspheres composed of vaterite using supercritical carbon dioxide in aqueous media, without surfactants. We show that the reaction in alkaline media rapidly conducts to the formation of microspheres with an average diameter of 5 µm. SEM, TEM and AFM observations reveal that the microspheres have a hollow core of around 0.7 µm width and are composed of nanograins with an average diameter of 40 nm. These nanograins are responsible for the high specific surface area of 16 m² g⁻¹ deduced from nitrogen absorption/desorption isotherms, which moreover confers an important porosity to the microspheres. We believe this work may pave the way for the elaboration of a biomaterial with a large potential for therapeutic as well as diagnostic applications.

Coccolithophores of the Noëlaerhabdaceae family are covered by imbricated coccoliths, each composed of multiple calcite crystals radially distributed around the periphery of a grid. The factors that determine coccolith size remain obscure. Here, we used synchrotron-based three-dimensional Coherent X-ray Diffraction Imaging to study coccoliths of 7 species of Gephyrocapsa, Emiliania and Reticulofenestra with a resolution close to 30 nm. Segmentation of 45 coccoliths revealed remarkable size, mass and segment number variations, even within single coccospheres. In particular, we observed that coccolith mass correlates with grid perimeter which scales linearly with crystal number. Our results indirectly support the idea that coccolith mass is determined in the coccolith vesicle by the size of the organic base plate scale (OBPS) around which R-unit nucleation occurs every 110–120 nm. The curvation of coccoliths allows inference of a positive correlation between cell nucleus, OBPS and coccolith sizes.