Hydroxyapatite (HA) forms an essential constituent of human teeth and bone. Its distinctive characteristic features, such as bioactivity and osteoconductivity, make it an ideal candidate to be used as an implant coating in restorative dentistry and maxillofacial surgery for bone regeneration. However, low fracture toughness and brittleness are a few of the inherent features of HA, which limit its application in load-bearing areas. The potential of HA to engage its lattice structure with either partial or complete substitution with external ions has become an increasing area of research as this phenomenon has the potential to enhance the biological and functional properties of the material. Consequently, this review aimed to highlight the role of various substituted ions in dental applications. Data indicate that the newly formed HA-substituted biomaterials demonstrate enhanced remineralization and antimicrobial activity along with improved hardness. Ion-substituted HA offers a promising strategy for future clinical research as these materials may be incorporated into various dental products for therapeutic treatments.

Background: Dental caries remains a significant global health problem. One of the fundamental mechanisms underlying the development and progression of dental caries is the dynamic process of demineralisation/remineralisation. In vitro models have played a critical role in advancing our understanding of this process and identifying potential interventions to prevent or arrest dental caries. This literature review aims to provide a structured oversight of in vitro mineralisation models which have been used to study the tooth demineralisation/remineralisation process. Methods: Publications from 2019 to 2023 were screened to identify articles reporting the use of in vitro models to study the demineralisation/remineralisation of tooth caries. The included studies were methodologically assessed for their information on (i) substrate, (ii) lesion formation, and (iii) mineralisation models. Results: The most reported substrates used in the studies were human teeth along with bovine incisors. Acetic/lactic buffers were the most common solutions to induce caries lesions. pH cycling was the most frequently used mineralisation model for simulating the daily change within the oral environment. This review discussed the advantages and limitations of various approaches. Conclusions: Standardisation of in vitro mineralisation models is crucial for enabling effective comparison between studies and advancing caries research.

Dental caries or tooth decay is a preventable and multifactorial disease that affects billions of people globally and is a particular concern in younger populations. This decay arises from acid demineralisation of tooth enamel resulting in mineral loss from the subsurface. The remineralisation of early enamel carious lesions could prevent the cavitation of teeth. The enamel protein amelogenin constitutes 90% of the total enamel matrix protein in teeth and plays a key role in the biomineralisation of tooth enamel. The physiological importance of amelogenin has led to the investigation of the possible development of amelogenin-derived biomimetics against dental caries. We herein review the literature on amelogenin, its primary and secondary structure, comparison to related species, and its’ in vivo processing to bioactive peptide fragments. The key structural motifs of amelogenin that enable enamel remineralisation are discussed. The presence of several motifs in the amelogenin structure (such as polyproline, N- and C-terminal domains and C-terminal orientation) were shown to play a critical role in the formation of particle shape during remineralization. Understanding the function/structure relationships of amelogenin can aid in the rational design of synthetic polypeptides for biomineralisation, halting enamel loss and leading to improved therapies for tooth decay.

Large oral bone defects require grafting of bone blocks rather than granules to give physically robust, biocompatible and osteoconductive regeneration. Bovine bone is widely accepted as a source of clinically appropriate xenograft material. However, the manufacturing process often results in both reduced mechanical strength and biological compatibility. The aim of this study was to assess bovine bone blocks at different sintering temperatures and measure the effects on mechanical properties and biocompatibility. Bone blocks were divided into four groups; Group 1: Control (Untreated); Group 2: Initial boil for 6 h; Group 3: Boil 6 h followed by sintering at 550 °C for 6 h; Group 4: Boil 6 h followed by sintering at 1100 °C for 6 h. Samples were assessed for their purity, crystallinity, mechanical strength, surface morphology, chemical composition, biocompatibility and clinical handling properties. Statistical analysis was performed using one-way ANOVA and post-hoc Tukey’s tests for normally distributed and Friedman test for abnormally distributed quantitative data from compression tests and PrestoBlue™ metabolic activity tests. The threshold for statistical significance was set at p < 0.05. The results showed that higher temperature sintering (Group 4) removed all organic material (0.02% organic components and 0.02% residual organic components remained) and increased crystallinity (95.33%) compared to Groups 1–3. All test groups (Group 2–4) showed decreased mechanical strength (MPa: 4.21 ± 1.97, 3.07 ± 1.21, 5.14 ± 1.86, respectively) compared with raw bone (Group 1) (MPa: 23.22 ± 5.24, p <0.05), with micro-cracks seen under SEM in Groups 3 and 4. Group 4 had the highest biocompatibility (p < 0.05) with osteoblasts as compared to Group 3 at all time points in vitro. Clinical handling tests indicated that Group 4 samples could better withstand drilling and screw placement but still demonstrated brittleness compared to Group 1. Hence, bovine bone blocks sintered at 1100 °C for 6 h resulted in highly pure bone with acceptable mechanical strength and clinical handling, suggesting it is a viable option as a block grafting material.

Purpose: To compare the mechanical properties and fracture behaviour of laser-sintered/3D-printed cobalt chromium (LS CoCr) with soft-milled cobalt chromium (SM CoCr) to assess their suitability for use in high-stress areas in the oral cavity. Material and Method: Two computer-aided manufacturing methods were used to fabricate dumbbell specimens in accordance with the ASTM standard E8. Specimens were fractured using tensile testing and elastic modulus, and proof stress and ultimate tensile strength were calculated. Fracture surfaces were examined using scanning electron microscopy. Plate specimens were also fabricated for the examination of hardness and elastic modulus using nanoindentation. Unpaired t-test was used to evaluate statistical significance. Results: LS CoCr specimens were found to have significantly higher ultimate tensile strength (UTS) and proof stress (PS) (p < 0.05) but not a significantly higher elastic modulus (p > 0.05). Examination of the dumbbell fracture surfaces showed uniform structure for the LS CoCr specimens whilst the SM CoCr specimens were perforated with porosities; neither showed an obvious point of fracture. Nanoindentation also showed that LS CoCr specimens possessed higher hardness compared with SM CoCr specimens. Conclusion: LS CoCr and SM CoCr specimens were both found to exhibit uniformly dense structure; although porosities were noted in the SM CoCr specimens. LS CoCr specimens were found to have superior tensile properties, likely due to lack of porosities, however both had mean values higher than those reported in the literature for cast CoCr. Uniformity of structure and high tensile strength indicates that LS CoCr and SM CoCr fabricated alloys are suitable for long-span metallic frameworks for use in the field of prosthodontics.