The polyfunctional nature of chitosan enables its application as a polymer ligand not only for the recovery, separation, and concentration of metal ions, but for the fabrication of a wide spectrum of functional materials. Although unmodified chitosan itself is the unique cationic polysaccharide with very good complexing properties toward numerous metal ions, its sorption capacity and selectivity can be sufficiently increased and turned via chemical modification to meet requirements of the specific applications. In this review, which covers results of the last decade, we demonstrate how different strategies of chitosan chemical modification effect metal ions binding by O-, N-, S-, and P-containing chitosan derivatives, and which mechanisms are involved in binding of metal cation and anions by chitosan derivatives.

A new procedure was developed for preparation of chelate amino-containing polymer N-2-sulfoethyl chitosan by synthesis in a gel through the reaction between chitosan and sodium 2-bromoethanesulfonate, yielding a polymer with the degree of substitution of up to 0.5. The structure of the resulting polymers was confirmed by ¹H NMR spectroscopy. The sorption characteristics with respect to transition and alkaline-earth metal ions were determined for the cross-linked polymers.

Here, we discuss the applicability of (methylenebis(salicylaldehyde)—MbSA) for the fabrication of the stimuli-responsive N-carboxyethylchitosan (CEC) hydrogels with a tunable dissolution rate under physiological conditions. In comparison with non-covalent salicylimine hydrogels, MbSA cross-linking via covalent bis(‘imine clip’) and non-covalent hydrophobic interactions allowed the fabrication of hydrogels with storage moduli > 1 kPa at ten-fold lower aldehyde/CEC molar ratio with the preservation of pH- and amino-acid responsive behavior. Although MbSA-cross-linked CEC hydrogels were stable at neutral and weakly alkaline pH, their disassembly in cell growth medium (Dulbecco’s modified Eagle’s medium, DMEM) under physiological conditions was feasible due to transimination reaction with amino acids contained in DMEM. Depending on the cross-linking density, the complete dissolution time of the fabricated hydrogels varied from 28 h to 11 days. The cytotoxicity of MbSA cross-linked CEC hydrogels toward a human colon carcinoma cell line (HCT 116) and primary human dermal fibroblasts (HDF) was remarkably lower in comparison with CEC-salicylimine hydrogels. Fast gelation, relatively low cytotoxicity, and tunable stimuli-induced disassembly under physiological conditions make MbSA cross-linked CEC hydrogels promising for drug encapsulation and release, 3D printing, cell culturing, and other biomedical applications.