Solvent-free (SF) anodes with different carbon materials (graphite, hard carbon, and soft carbon) were fabricated to investigate the stability of different anodes with polytetrafluorethylene (PTFE) degradation. The graphite anode with large volume variation during the charge/discharge process showed poor cycle life performance, while hard carbon and soft carbon with low-volume expansion showed good cycle life. The SF hard carbon electrodes with a high loading of 10.7 mg/cm² revealed good long-term cycling performance similar to conventional slurry-casting (CSC) electrodes. It demonstrated nearly 90% capacity retention after 120 cycles under a current of 1/3 C with LiNi_0.5Co_0.2Mn_0.3O₂ (NCM523) as cathode in coin cell. The rate capability of the high-loading SF electrodes also is comparable to the CSC electrodes. The high stability of SF hard carbon and soft carbon anodes was attributed to its low-volume variation, which could maintain their integrity even though PTFE was defluorinated to amorphous carbon irreversibly. However, the reduced amorphous carbon cannot tolerate huge volume variation of graphite during cycling, resulting in poor stability.

Electrocatalytic CO₂ reduction (ECR) is an attractive approach to convert atmospheric CO₂ to value-added chemicals and fuels. However, this process is still hindered by sluggish CO₂ reaction kinetics and the lack of efficient electrocatalysts. Therefore, new strategies for electrocatalyst design should be developed to solve these problems. Two-dimensional (2D) materials possess great potential in ECR because of their unique electronic and structural properties, excellent electrical conductivity, high atomic utilization and high specific surface area. In this review, we summarize the recent progress on 2D electrocatalysts applied in ECR. We first give a brief description of ECR fundamentals and then discuss in detail the development of different types of 2D electrocatalysts for ECR, including metal, graphene-based materials, transition metal dichalcogenides (TMDs), metal–organic frameworks (MOFs), metal oxide nanosheets and 2D materials incorporated with single atoms as single-atom catalysts (SACs). Metals, such as Ag, Cu, Au, Pt and Pd, graphene-based materials, metal-doped nitric carbide, TMDs and MOFs can mostly only produce CO with a Faradic efficiencies (FE) of 80~90%. Particularly, SACs can exhibit FEs of CO higher than 90%. Metal oxides and graphene-based materials can produce HCOOH, but the FEs are generally lower than that of CO. Only Cu-based materials can produce high carbon products such as C₂H₄ but they have low product selectivity. It was proposed that the design and synthesis of novel 2D materials for ECR should be based on thorough understanding of the reaction mechanism through combined theoretical prediction with experimental study, especially in situ characterization techniques. The gap between laboratory synthesis and large-scale production of 2D materials also needs to be closed for commercial applications.

Lithium-ion capacitors (LiC) are promising hybrid devices bridging the gap between batteries and supercapacitors by offering simultaneous high specific power and specific energy. However, an indispensable critical component in LiC is the capacitive cathode for high power. Activated carbon (AC) is typically the cathode material due to its low cost, abundant raw material for production, sustainability, easily tunable properties, and scalability. However, compared to conventional battery-type cathodes, the low capacity of AC remains a limiting factor for improving the specific energy of LiC to match the battery counterparts. This review discusses recent approaches for achieving high-performance LiC, focusing on the AC cathode. The strategies are discussed with respect to active material property modifications, electrodes, electrolytes, and cell design techniques which have improved the AC’s capacity/capacitance, operating potential window, and electrochemical stability. Potential strategies and pathways for improved performance of the AC are pinpointed.

Li-ion capacitors (LICs) are designed to achieve high power and energy densities using a carbon-based material as a positive electrode coupled with a negative electrode often adopted from Li-ion batteries. However, such adoption cannot be direct and requires additional materials optimization. Furthermore, for the desired device’s performance, a proper design of the electrodes is necessary to balance the different charge storage mechanisms. The negative electrode with an intercalation or alloying active material must provide the high rate performance and long-term cycling ability necessary for LIC functionality—a primary challenge for the design of these energy-storage devices. In addition, the search for new active materials must also consider the need for environmentally friendly chemistry and the sustainable availability of key elements. With these factors in mind, this review evaluates advanced and emerging materials used as high-rate anodes in LICs from the perspective of their practical implementation.

The galvanostatic charge–discharge (GCD) behaviour of silicon (Si) is known to depend strongly on morphology, cycling conditions and electrochemical environment. One common method for analysing GCD curves is through differential capacity, but the data processing required necessarily degrades the results. Here we present a method of extracting empirical information from the delithiation step in GCD data for Si at C-rates above equilibrium conditions. We find that the function is able to quickly and accurately determine the best fit to historical half-cell data on amorphous Si nanowires and thin films, and analysis of the results reveals that the function is capable of distinguishing the capacity contributions from the Li${}_{3.5}$Si and Li${}_2$Si phases to the total capacity. The method can also pick up small differences in the phase behaviour of the different samples, making it a powerful technique for further analysis of Si data from the literature. The method was also used for predicting the size of the reservoir effect (the apparent amount of Li remaining in the electrode), making it a useful technique for quickly determining voltage slippage and related phenomena. This work is presented as a starting point for more in-depth empirical analysis of Si GCD data.

EIS is performed on high loading commercial Si electrodes half cells are found to be strongly dependent on the Li counter electrode. Li is found to dominate the EIS spectrum of Si half cells at potentials below 0.07 V and above 0.48 V vs. Li/Li⁺.