The response of a graphene-based humidity sensor is considered as a function of film structures. Analysis of the resistance changes due to water molecule adsorption on the graphene or multi-layer graphene (MLG) surface is performed for films with different structures and resistivities from hundreds of ohms/sq to hundreds of kilo-ohms/sq. The results revealed possible increase, decrease and non-monotonous behavior of resistance with changes in film structure. Adsorption of water molecules at grain boundary defects is assumed to lead to an increase in film resistivity due to the donor property of water and the p-type conductivity of graphene. Another type of conductive center with a higher capture cross-section is realized in the case of water molecule adsorption at edge defects in MLG films (the formation of conductive chains with ionic conductivity). If these chains form a continuous network the film resistivity decreases. The result of the competition between the opposite effects of the conductivity compensation and formation of the water-based conductive chains depends on the film structure and determines the response of humidity sensors. Sensor sensitivity is found to increase when only one type of defect determines water adsorption (edge defects or grain boundary defects).

In this study, we compared the trap density distributions, $D_{\mathrm{it}},$ in the band gap of silicon at the Si/thermal ${\mathrm{SiO}}_{\mathrm{2}}$ interface and at the bonded interface of the silicon–on–insulator structure, deduced from deep level transient spectroscopy measurements. The trap energies for the bonded ${\mathrm{Si/SiO}}_{\mathrm{2}}$ interface are localized in the range from $E_c\text{–0.17}$ to $E_c\text{–0.37\hspace{0.05em}}\mathrm{eV}.$ The lack of the transient ${\mathrm{SiO}}_x$ layer at the bonded interface is suggested to lead to a relatively narrow interval of trap energies.

Two-dimensional nanomaterials such as graphene can provide various functional properties to textiles, which have great potential in sportswear, healthcare etc. In this study, the properties of nylon and cotton-based electronic textiles coated with reduced graphene oxide are investigated. After reduction of graphene oxide coating in hydrazine vapor, e-textiles with a resistance of ~350 Ω/sq for nylon, and ~1 kΩ/sq for cotton were obtained. Cyclic mechanical bending tests of samples showed that the resistance increases during bending up to 10–20%. The use of bovine serum albumin as an adhesive layer improved the wash stability for samples with nylon up to 40 washing cycles. The use of BF-6 glue as a protective layer reduced changes in resistance during bending, and improved wash stability of cotton samples. It was shown that the resistance of the obtained samples is sensitive to changes in temperature and humidity. In addition, obtained e-textiles attached to a person’s wrist were able to measure heart rate. Thus, the obtained electronic textiles based on cotton and nylon coated with reduced graphene oxide demonstrates good characteristics for use as sensors for monitoring vital signs.