This study aimed to determine the effects of design parameters, including the liquid/solid ratio (L/S), Na₂SiO₃/NaOH weight ratio, and curing temperature, on class F fly ash-based geopolymer composites. For this purpose, two disparate sources of fly ash were supplied from Çatalağzı (FA) and İsken Sugözü (FB) Thermal Power Plants in Turkey. Two different L/S ratios of 0.2 and 0.4 were used. The Na₂SiO₃/NaOH ratios in the alkaline solutions were 1, 1.5, 2, 2.5, and 3 by weight for each type of geopolymer mixture. Then, 40 different mixes were cured at two specific temperatures (70 °C and 100 °C) for 24 h and then preserved at room temperature until testing. Thereafter, the physical water absorption properties, apparent porosity, and bulk density were examined at 28 days on the hardened mortars. Additionally, compressive and flexural tests were applied to the geopolymers at 7, 28, and 90 days. It was found that the highest compressive strength was 60.1 MPa for the geopolymer manufactured with an L/S of 0.2 and Na₂SiO₃/NaOH ratio of 2. Moreover, the best thermal curing temperature for obtaining optimal strength characteristics was 100 °C for the FB.

Bu çalışmada, atık cam tozu (ACT) ve öğütülmüş yüksek fırın cürufunun (YFC) kendiliğinden yerleşen harcın (KYH) taze, mekanik ve durabilite özellikleri üzerine etkilerinin karşılaştırılması amaçlanmıştır. Mineral katkı malzemesi olarak, atık cam tozu) ve yüksek fırın cürufu içeren kendiliğinden yerleşen harçlar 0.40 sabit su/bağlayıcı oranı, 24.5±0.5 cm sabit bir yayılma çapı ve yüksek oranda su azaltıcı kimyasal katkı (süper akışkanlaştırıcı) kullanılarak üretilmiştir. İlk aşamada mineral katkı malzemesi içermeyen referans KYH üretimi yapılmıştır. İki gruptan oluşan bu çalışmada, birinci grupta ACT karışımları, ACT’nin çimento yerine %5, %10, %15 ve %20 oranlarında kullanılmasıyla tasarlanmıştır.İkinci grupta ise YFC karışımları, çimentonun %20’si yerine ACT ve YFC kullanılarak üretilmiştir. Böylece ikinci grup karışımları, YFC’nin ACT ile %5,%10, %15 ve %20 oranlarında yer değiştirmesi ile elde edilmiştir. Toplamda 9 farklı karışımın üretimi yapılmıştır. Taze özellikleri belirlemek için mini yayılma çapı ve mini v-hunisi deneyleri yapılmıştır. Mekanik özellikleri tespit etmek için 3., 7., 28. ve 56. günlerde basınç ve eğilme dayanımı ile ultrasonik titreşim hızı deneyleri uygulanmıştır. Bunlara ek olarak 28. ve 56. günlerde yapılan kılcal su geçirimliliği, hızlı klor geçirimliliği deneyleriyle de durabilite özellikleri belirlenmiştir. KYH’de, çimento yerine kullanılan ACT mineralinin KYH’nin taze, mekanik ve durabilite özelliklerini geliştirdiği gözlemlenmiştir. Cam tozu ve cürufun karşılaştırıldığı ikinci grup karışımlarda ise ACT’nin YFC’ye göre daha avantajlı olduğu tespit edilmiştir. Yüksek fırın cürufu yerine kullanılan cam tozu miktarının artmasıyla, KYH’lerin taze, mekanik ve durabilite özellikleri iyileşmiştir.

En tr This study has been carried out to investigate the effect of Osmaniye basic pumice on the workability characteristics of self-compacting concrete (SCC). Self-compacting concrete incorporated basic pumice (SCCB) with a constant water / binder ratio (cement + fly ash) of 0.32 was produced at a fixed slump flow diameter of 690±20 mm by adjusting the amount of High-Range-Water-Reducing-Admixture (HRWRA). First, control concrete without basic pumice was produced at a constant water/binder ratio and then basic pumice replacing the coarse aggregate in the proportions of 20%, 30%, 40%, 50% and 60% was added to the mixture. To identify effects of basic pumice on properties in the fresh and hardened state of SCCB, slump flow diameter, T₅₀₀ flow time, V-funnel flow time, L-box height ratio and 28-day compressive strength tests were conducted. Increasing amount of the basic pumice in the SCC resulted in a gradual decrease of workability. Therefore, SCCB has been manufactured by adding basic pumice up to 60%. Due to the specific weight of basic pumice lower than that of crushed stone, compressive strength of SCC showed a decrease of 23%. Bu çalışma kendiliğinden yerleşen beton (KYB) üretiminde Osmaniye bazik pomzasının işlenebilirliğe olan etkisini araştırmak amacıyla gerçekleştirilmiştir. Bazik pomza katkılı kendiliğinden yerleşen beton (KYBB) üretimi 0,32 sabit su/bağlayıcı (çimento + uçucu kül) oranında, 690±20 mm sabit bir çökme akışıyla, yüksek oranda su azaltıcı katkı (akışkanlaştırıcı) kullanılarak gerçekleştirilmiştir. İlk olarak bazik pomza hiç katılmaksızın kontrol betonu sabit su/bağlayıcı oranı ile dökülmüş ve daha sonra bazik pomza %20, %30, %40, %50 ve %60 oranlarında her defasında iri agreganın yerine ikame edilerek karışıma eklenmiştir. Bazik pomzanın KYBB’lerin taze ve sertleşmiş haldeki özellikleri üzerine etkilerini tespit etmek amacıyla taze haldeki betonun çökme yayılma tablasında akış çapı ve T₅₀₀ süresi, V hunisinde boşalma süresi, L kutusunda yükseklik oranı testleri ve 28 günlük basınç dayanımı testi yapılmıştır. KYBB’de kullanılan bazik pomza miktarı arttıkça işlenebilirliğin giderek azaldığı tespit edilmiştir. Bu nedenle en fazla %60 oranında bazik pomza kullanılarak KYBB üretilebilmiştir. KYB’nin basınç dayanımı ise bazik pomzanın özgül ağırlığının kırma taştan düşük olmasından dolayı %23 oranında bir azalma göstermiştir.