Ultrasonic-hydrothermal and hydrothermal treatment was used for synthesis of nanocrystalline zirconia, titania, nickel and nickel-zinc ferrites powders from precipitated amorphous zirconyl, titanyl, binary nickel-iron and ternary nickel-zinc-iron hydroxides, respectively. Resulted nanopowders were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), nitrogen adsorption (BET), and magnetic susceptibility measurements. It was established that ultrasonically assisted hydrothermal treatment of amorphous zirconyl and titanyl gels results in significant rise of the rate of ZrO2 and TiO2 crystallization and promotes formation of thermodynamically stable monoclinic zirconia, but does not affect the microstructure and mean particles size of resulting nanopowders. Ultrasonic-hydrothermal processing of co-precipitated amorphous nickel, zinc and iron hydroxides favours formation of nanocrystalline ferrite powders with narrower particle size distribution.

Generalized dependence of unit cell parameter and oxygen non-stoichiometry on the particle size of nanocrystalline ceria synthesized by a wide variety of solution-based methods was established.

This work demonstrates the possibility of preparing solid solutions in the (MgGa2O4) x(MgFe2O4)1 − xsystem by pyrohydrolytic and solid-phase methods. It is shown that the products obtained have...