Microplastics are found in marine and freshwater environments; however, their specific sources are not yet well understood. Understanding sources will be of key importance in efforts to reduce emissions into the environment. We examined the emissions of microfibers from domestic washing of a new microfiber polyester fleece textile. Analyzing released fibers collected with a 200 μm filter during 10 mild, successive washing cycles showed that emission initially decreased and then stabilized at approx. 0.0012 wt%. This value is our estimation for the long-term release of fibers during each washing. Use of detergent and softener did not significantly influence emission. Release of fibers during tumble drying was approx. 3.5 times higher than during washing.

Microplastics (MPs) are persistent tiny pieces of plastic material in the environment that are capable of adsorbing environmental organic pollutants from their surroundings. The interaction of MPs with organic pollutants alters their environmental behavior, i.e., their adsorption, degradation and toxicity, etc. Polyethylene (PE) is the most widely used plastic material. The environmental weathering of PE results in changes to its surface chemistry, making the polymer a much better vector for organic pollutants than virgin PE. In this study, a laboratory-accelerated weathering experiment was carried out with a virgin PE film and an oxidatively degradable PE (OXO-PE) film, i.e., PE modified by the addition of a pro-oxidant catalyst. The degradation of PE and OXO-PE was assessed through Fourier transform infra-red (FTIR) spectroscopy and their wettability was measured by contact angle (CA) measurements. Their thermal properties and morphology were studied using thermogravimetric analyses (TGA) and scanning electron microscopy (SEM), respectively. Further, the adsorption of two model organic pollutants onto weathered and virgin PE was analyzed. Triclosan (TCS) and methylparaben (MeP) were chosen as model organic pollutants for the adsorption experiment due to their frequent use in the cosmetics industry, their uncontrolled release into the environment and their toxicity. The adsorption of both model pollutants onto PE and OXO-PE MP was analyzed by using gas chromatography with a flame ionization detector (GC-FID). The adsorption of MeP onto OXO-PE was higher than onto PE MPs. However, TCS showed insignificant adsorption onto PE and OXO-PE. When both pollutants were present simultaneously, the adsorption of TCS onto both PE and OXO-PE was significantly influenced by the presence of MeP. This result demonstrates that the adsorption behavior of one pollutant can be significantly altered by the presence of another pollutant. Both the effect of weathering on the adsorption of organic pollutants as well as the interaction between organic pollutants adsorbing onto MPs is highly relevant to actual MP pollution in the environment, where MPs are exposed to weathering conditions and mixtures of organic pollutants.

Liquefied wood (LW) prepared in a microwave process was applied as a novel; inexpensive precursor feedstock for incorporation of (R)-3-hydroxyvalerate (3HV) into polyhydroxyalkanoate (PHA) biopolyesters in order to improve the biopolyester’s material quality; Cupriavidus necator was applied as microbial production strain. For proof of concept, pre-experiments were carried out on a shake flask scale using different mixtures of glucose and LW as carbon source. The results indicate that LW definitely acts as a 3HV precursor, but, at the same time, displays toxic effects on C. necator at concentrations exceeding 10 g/L. Based on these findings, PHA biosynthesis under controlled conditions was performed using a fed-batch feeding regime on a bioreactor scale. As major outcome, a poly(3HB-co-0.8%-3HV) copolyester was obtained displaying a desired high molar mass of M_w = 5.39 × 10⁵ g/mol at low molar-mass dispersity (Đ_M of 1.53), a degree of crystallinity (X_c) of 62.1%, and melting temperature T_m (176.3 °C) slightly lower than values reported for poly([R]-3-hydroxybutyrate) (PHB) homopolyester produced by C. necator; thus, the produced biopolyester is expected to be more suitable for polymer processing purposes.