Superparamagnetic iron oxide nanoparticles (SPION) have a great potential in both diagnostic and therapeutic applications as they provide contrast in magnetic resonance imaging techniques and allow magnetic hyperthermia and drug delivery. Though various types of SPION are commercially available, efforts to improve the quality of SPION are highly in demand. Here, we describe a strategy for optimization of SPION synthesis under microfluidics using the coprecipitation approach. Synthesis parameters such as temperature, pH, iron salt concentration, and coating materials were investigated in continuous and segmented flows. Continuous flow allowed synthesizing particles of a smaller size and higher stability than segmented flow, while both conditions improved the quality of particles compared to batch synthesis. The most stable particles were obtained at a synthesis condition of 6.5 M NH₄OH base, iron salt (Fe²⁺/Fe³⁺) concentration ratio of 4.3/8.6, carboxymethyl dextran coating of 20 mg/mL, and temperature of 70 °C. The synthesized SPION exhibited a good efficiency in labeling of human platelets and did not impair cells. Our study under flow conditions provides an optimal protocol for the synthesis of better and biocompatible SPION that contributes to the development of nanoparticles for medical applications.

Platelet-surface interaction is of paramount importance in biomedical applications as well as in vitro studies. However, controlling platelet-surface activation is challenging and still requires more effort as they activate immediately when contacting with any nonphysiological surface. As hydrogels are highly biocompatible, in this study, we developed agarose and gelatin-based hydrogel films to inhibit platelet-surface adhesion. We found promising agarose films that exhibit higher surface wettability, better controlled-swelling properties, and greater stiffness compared to gelatin, resulting in a strong reduction of platelet adhesion. Mechanical properties and surface wettability of the hydrogel films were varied by adding magnetite (Fe₃O₄) nanoparticles. While all of the films prevented platelet spreading, films formed by agarose and its nanocomposite repelled platelets and inhibited platelet adhesion and activation stronger than those of gelatin. Our results showed that platelet-surface activation is modulated by controlling the properties of the films underneath platelets and that the bioinert agarose can be potentially translated to the development of platelet storage and other medical applications.

Freestanding multilayer films prepared by layer‐by‐layer technique have attracted interest as promising materials for wound dressings. The goal is to fabricate freestanding films using chitosan (CHI) and alginate (ALG) including subsequent crosslinking to improve the mechanical properties of films while maintaining their biocompatibility. Three crosslinking strategies are investigated, namely use of calcium ions for crosslinking ALG, 1‐ethyl‐3‐(‐3‐dimethylaminopropyl) carbodiimide combined with N‐hydroxysuccinimide for crosslinking ALG with CHI, and Genipin for crosslinking chitosan inside the films. Different characteristics, such as surface morphology, wettability, swelling, roughness, and mechanical properties are investigated showing that films became thinner, exhibited rougher surfaces, had lower water uptake, and increased mechanical strength after crosslinking. Changes of wettability are moderate and dependent on the crosslinking method. In vitro cytotoxicity and cell attachment studies with human dermal fibroblasts show that freestanding CHI‐ALG films represent a poorly adhesive substratum for fibroblasts, while studies using incubation of plastic‐adherent fibroblast beneath floating films show no signs of cytotoxicity in a time frame of 7 days. Results from cell experiments combined with film characteristics after crosslinking, indicate that crosslinked freestanding films made of ALG and CHI may be interesting candidates for wound dressings.