The paper deals with the correlation between the internal structure and dynamics of polyelectrolyte multilayers on one hand and their functional properties on the other hand. It considers different concepts of multilayer formation like driving forces, adsorption kinetics, mode of growth and stability aspects. A further focus is the control of internal structure and dynamics which is of high impact with respect to the design of stimuli-responsive material.

The swelling/deswelling behaviour of microgel particles in the bulk and at the surface was studied and correlated to their mechanical properties. We focused on two kinds of particles: pure PNIPAM and PNIPAM-co-AAc particles. It was shown that the two step volume phase transition found for PNIPAM-co-AAc particles in the bulk disappears after the adsorption at the surface and only a one step transition was identified. The transition temperature increased strongly with increasing the co-monomer content. The dependence of the Young’s modulus of the adsorbed microgel particles on the temperature and the co-monomer content was discussed. The investigations were performed via DLS and SFM.

This study addresses the effect of ionic strength and type of ions on the structure and water content of polyelectrolyte multilayers. Polyelectrolyte multilayers of poly(sodium-4-styrene sulfonate) (PSS) and poly(diallyl dimethyl ammonium chloride) (PDADMAC) prepared at different NaF, NaCl and NaBr concentrations have been investigated by neutron reflectometry against vacuum, H₂O and D₂O. Both thickness and water content of the multilayers increase with increasing ionic strength and increasing ion size. Two types of water were identified, “void water” which fills the voids of the multilayers and does not contribute to swelling but to a change in scattering length density and “swelling water” which directly contributes to swelling of the multilayers. The amount of void water decreases with increasing salt concentration and anion radius while the amount of swelling water increases with salt concentration and anion radius. This is interpreted as a denser structure in the dry state and larger ability to swell in water (sponge) for multilayers prepared from high ionic strengths and/or salt solution of large anions. No exchange of hydration water or replacement of H by D was detected even after eight hours incubation time in water of opposing isotopic composition.