The durability of natural fibres as reinforcement in geopolymer composites continues to be a matter of concern due to the alkalinity of activators of geopolymer matrices. The alkaline environment is the main reason for natural fibres degradation in cementitious matrices. This paper presents the influence of nano silica (NS) on the durability and mechanical performance of geopolymer composites that are reinforced with flax fabric (FF). The durability investigations were conducted after the storage of samples at ambient temperature for 32 weeks. The study revealed that the addition of nano silica has a positive influence on the physical and mechanical properties of these composites. The presence of NS accelerated the geopolymeric reaction and lowered the alkalinity of the system, thus reducing the degradation of flax fibres.

This paper presents the effects of various nanosilica (NS) contents on the mechanical properties of polyvinyl alcohol (PVA) fiber-reinforced geopolymer composites (PVA-FRGC). Microstructure analysis with X-ray diffraction (XRD) and scanning electron microscopy (SEM) was used to characterize the geopolymer composites. The results showed that the mechanical properties in terms of compressive strength, impact strength, and flexural behavior were improved due to the addition of NS to the PVA-FRGC. The optimum NS content was 1.0 to 2.0 wt%, which exhibited highest improvement in the above mechanical properties. Microstructure analysis showed that the addition of NS up to an optimum level densified the microstructure of the matrix as well as the PVA fiber–geopolymer matrix interface.