This paper aims to examine the effect of cellulose nanocrystals (CNC) on the hydration, transport behavior, and microstructure of cement mixtures. The addition of CNC delayed hydration at an early age but improved hydration at later ages. A small increase in the electrical resistivity of the cement mixtures with CNC was observed. Statistical nanoindentation showed a small tendency to a larger volume fraction of high density calcium-silicate-hydrate (C-S-H) and a smaller volume fraction of low-density C-S-H in the mixture with CNC.

This paper investigates the effect of curing temperature on the hydration, microstructure, compressive strength, and transport of cement pastes modified with TiO₂ nanoparticles. These characteristics of cement pastes were studied using non-evaporable water content measurement, X-ray diffraction (XRD), compressive strength test, electrical resistivity and porosity measurements, and scanning electron microscopy (SEM). It was shown that temperature enhanced the early hydration. The cement pastes cured at elevated temperatures generally showed an increase in compressive strength at an early age compared to the cement paste cured at room temperature, but the strength gain decreased at later ages. The electrical resistivity of the cement pastes cured at elevated temperatures was found to decrease more noticeably at late ages compared to that of the room temperature cured cement paste. SEM examination indicated that hydration product was more uniformly distributed in the microstructure of the cement paste cured at room temperature compared to the cement pastes cured at elevated temperatures. It was observed that high temperature curing decreased the compressive strength and electrical resistivity of the cement pastes at late ages in a more pronounced manner when higher levels of TiO₂ nanoparticles were added.

Inspired by nature, this paper investigates the effect of biomolecules, such as amino acids and proteins, on the nanostructure and mechanical stiffness of calcium-silicate-hydrate (C-S-H). Amino acids with distinct functional groups, and proteins with different structures and compositions were used in the synthesis of the C-S-H nanocomposite. The atomic structure was examined using X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR). The morphology was investigated using scanning electron microscopy (SEM) and atomic force microscopy (AFM). AFM nanoindentation was used to evaluate the Young’s modulus of the modified C-S-H. Positively charged, H-bond forming and hydrophobic amino acids were shown to influence the atomic structure of C-S-H. The effect of negatively charged amino acid on atomic structure was more pronounced at higher C/S ratio. A noticeable increase in silicate polymerization of C-S-H modified with proteins at high C/S ratio was observed. The microscopic examination demonstrated a globular morphology for all samples except for C-S-H modified with hemoglobin, which showed a platelet morphology. The Young’s modulus of C-S-H with amino acids and proteins showed a general reduction compared to that of the control C-S-H.