Polymer composites are being considered for numerous thermal applications because of their inherent benefits, such as light weight, corrosion resistance, and reduced cost. In this work, the microstructural, thermal, and mechanical properties of a 3D printed polymer composite with high thermal conductivity are examined using multiple characterization techniques. Infrared spectroscopy and X-ray diffraction reveal that the composite contains a polyphenylene sulfide matrix with graphitic fillers, which is responsible for the high thermal conductivity. Furthermore, differential scanning calorimetry determines that the glass transition and melting point of the composite are 87.6 °C and 285.6 °C, respectively. Thermogravimetric analysis reveals that the composite is thermally stable up to ~400 °C. Creep tests are performed at different isotherms to evaluate the long-term performance of the composite. The creep result indicates that the composite can maintain mechanical integrity when used below its glass transition temperature. Nanoindentation tests reveal that modulus and hardness of the composite is not significantly influenced by heating or creep conditions. These findings indicate that the composite is potentially suitable for heat exchanger applications.

Magnetocaloric alloys are an important class of materials that enable non-vapor compression cycles. One promising candidate for magnetocaloric systems is LaFeMnSi, thanks to a combination of factors including low-cost constituents and a useful curie temperature, although control of the constituents’ phase distribution can be challenging. In this paper, the effects of composition and high energy ball milling on the particle morphology and phase stability of LaFe_11.71-xMn_xSi_1.29H_1.6 magnetocaloric powders were investigated. The powders were characterized with optical microscopy, dynamic light scattering, X-ray diffraction (XRD), and differential scanning calorimetry (DSC). It was found that the powders retained most of their original magnetocaloric phase during milling, although milling reduced the degree of crystallinity in the powder. Furthermore, some oxide phases (<1 weight percent) were present in the as-received and milled powders, which indicates that no significant contamination of the powders occurred during milling. Finally, the results indicated that the Curie temperature drops as Fe content decreases (Mn content increases). In all of the powders, milling led to an increase in the Curie temperature of ~3–6 °C.

The heat transfer rate of magnetocaloric regenerators is a topic of extensive research and the cyclability of these regenerators is critical to the operation of systems with a high coefficient of performance (e.g., potentially >22, significantly higher than typical vapor compression cooling technologies). To enable a high operating frequency that will result in a high specific cooling power, the heat transfer fluid should have high thermal conductivity and lower specific heat, i.e., higher thermal diffusivity. Eutectic metal alloys possess these qualities, such as gallium–indium–tin (Galinstan), whose thermal diffusivity has been found to be approximately an order of magnitude higher than water. For this study, the effects of eutectic liquid Galinstan exposure on the phase stability of LaFe_13−x−yMn_xSi_yH_1.6 magnetocaloric powders in an active magnetic regenerator device were investigated. The powders were characterized before and after exposure to Galinstan using X-ray diffraction, in which the phases were determined using the Rietveld refinement technique and X-ray fluorescence. It was found that after Galinstan exposure, hydrogen containing phases were present in the powder, suggesting that the hydrogen was lost from the magnetocaloric phase. The magnetocaloric phase degradation indicates that the powder was incompatible with the Galinstan metal in an environment with moisture.