Copper nanoparticles (CuNP) were obtained by a green synthesis method using cotton textile fibers and water as solvent, avoiding the use of toxic reducing agents. The new synthesis method is environmentally friendly, inexpensive, and can be implemented on a larger scale. This method showed the cellulose capacity as a reducing and stabilizing agent for synthetizing Cellulose–Copper nanoparticles (CCuNP). Nanocomposites based on CCuNP were characterized by XRD, TGA, FTIR and DSC. Functional groups present in the CCuNP were identified by FTIR analysis, and XRD patterns disclosed that nanoparticles correspond to pure metallic Cu°, and their sizes are at a range of 13–35 nm. Results demonstrated that CuNPs produced by the new method were homogeneously distributed on the entire surface of the textile fiber, obtaining CCuNP nanocomposites with different copper wt%. Thus, CuNPs obtained by this method are very stable to oxidation and can be stored for months. Characterization studies disclose that the cellulose crystallinity index (CI) is modified in relation to the reaction conditions, and its chemical structure is destroyed when nanocomposites with high copper contents are synthesized. The formation of CuO nanoparticles was confirmed as a by-product, through UV spectroscopy, in the absorbance range of 300–350 nm.

Copper nanoparticles (CuNPs) functionalized with polyethyleneimine (PEI) and 4-aminobutyric acid (GABA) were used to obtain composites with isotactic polypropylene (iPP). The iPP/CuNPs composites were prepared at copper concentrations of 0.25–5.0 wt % by melt mixing, no evidence of oxidation of the CuNP was observed. Furthermore, the release of copper ions from iPP/CuNPs composites in an aqueous medium was studied. The release of cupric ions was higher in the composites with 2.5 and 5.0 wt %. These composites showed excellent antibacterial activity (AA) toward Pseudomona aeruginosa (P. aeruginosa) and Staphylococcus aureus (S. aureus). The incorporation of CuNP into the iPP polymeric matrix slightly decreased the thermal stability of the composite material but improved the crystallinity and the storage modulus. This evidence suggests that CuNPs could work as nucleating agents in the iPP crystallization process. The iPP/CuNPs composites presented better AA properties compared to similar composites reported previously. This behavior indicates that the new materials have great potential to be used in various applications that can be explored in the future.

Copper nanoparticles (Cu‐NPs) with sizes lower than 31 nm were prepared by wet chemical reduction using copper sulfate solution, hydrazine, and mixture of allylamine (AAm) and polyallylamine (PAAm) as stabilizing agents. The use of AAm/PAAm mixture leads to the formation of Cu and CuO nanoparticles. The resulting nanostructures were characterized by XRD, TGA, and TEM. The average particle diameters were determined by the Debye‐Scherrer equation. Analysis by TGA, TEM, GS‐MS, and ¹HNMR reveals that synthesized NPs with AAm presented a coating with similar characteristics to NPs with PAAm, suggesting that AAm underwent polymerization during the synthesis. The synthesis of NPs using AAm could be a good alternative to reduce production costs.