Because of their importance in a variety of interdisciplinary study domains, Schiff-base ligands have performed a significant role in the evolution of contemporary coordination chemistry. This almost-comprehensive review covers all the aspects and properties of complexes, starting from the Schiff-base ligands. Our work is centered on the eloquent advances that have been developed since 2015, with special consideration to recent developments. Schiff-base ligands and their complexes are adaptable compounds obtained from the condensation of two compounds: a carbonyl with an amino. The correspondent metal complexes have been shown to have antifungal, antibacterial, antioxidant, antiproliferative, and antiviral properties. This review begins with a short introduction to Schiff-base ligands and their metal complexes. It stands out in the recent advancements in the Schiff-base coordination chemistry domain and its future prospects as a potential bioactive core. Additionally, the review contains knowledge about the antioxidant, redox, and catalytic activities of the Schiff-base complexes, with important future applications in the obtaining of new compounds and materials.

Siloxane-based elastomers are some of the most sought-after materials for the construction of actuators and equipment for energy harvesting devices. This article focuses on changes of the mechanical (breaking stress, breaking strain, Young’s modulus) and dielectric properties for elastomers prepared with silicones, induced by the variation of molecular weight of the matrix, with three different silicone polymers having 60,000 g/mol, 150,000 g/mol, and 450,000 g/mol (from GPC measurements). Multiple siloxane elastomers were crosslinked with methyltriacetoxysilane using the sol-gel route. The dielectric permittivity values of the elastomers were also enhanced with two different complex structures containing siloxane bond and 3d transition metals as filler materials for polydimethylsiloxane polymers with various molecular weights. The dielectric spectroscopy tests demonstrated a small decrease (5%) for the values of the dielectric permittivity in relation to increased molecular weight of the siloxane polymer, both for samples prepared with pure polymer and for samples with metal complexes. The samples of nanocomposites showed a >50% increase of dielectric permittivity values relative to samples prepared of pure siloxane elastomer. The thermal tests demonstrated that the nanocomposites retained thermal stability similar with samples prepared of pure siloxane elastomer. The behavior under controlled conditions of humidity showed a trend of increased water vapor sorption with increasing molecular weight but an overall hydrophobic stable character of nanocomposites.