Excessive use of nitrogen fertilizer in intensively managed agriculture has resulted in abundant accumulation of nitrate in soil, which limits agriculture sustainability. How to reduce nitrate content is the key to alleviate secondary soil salinization. However, the microorganisms used in soil remediation cause some problems such as weak efficiency and short survival time. In this study, seaweed polysaccharides were used as stimulant to promote the rapid growth and safer nitrate removal of denitrifying bacteria. Firstly, the growth rate and NO₃⁻-N removal capacity of three kinds of denitrifying bacteria, Bacillus subtilis (BS), Pseudomonas stutzeri (PS) and Pseudomonas putida (PP), were compared. The results showed that Bacillus subtilis (BS) had a faster growth rate and stronger nitrate removal ability. We then studied the effects of Enteromorpha linza polysaccharides (EP), carrageenan (CA), and sodium alginate (AL) on growth and denitrification performance of Bacillus subtilis (BS). The results showed that seaweed polysaccharides obviously promoted the growth of Bacillus subtilis (BS), and accelerated the reduction of NO₃⁻-N. More importantly, the increased NH₄⁺-N content could avoid excessive loss of nitrogen, and less NO₂⁻-N accumulation could avoid toxic effects on plants. This new strategy of using denitrifying bacteria for safely remediating secondary soil salinization has a great significance.

In this study, a hollow tubulous-shaped In₂O₃ derived from MIL (MIL-68 (In)) exhibited an enhanced specific surface area compared to MIL. To further sensitize In₂O₃, ZnIn₂S₄ was grown in situ on the derived In₂O₃. The 40In₂O₃/ZnIn₂S₄ composite (1 mmol ZnIn₂S₄ loaded on 40 mg In₂O₃) exhibited degradation rates of methyl orange (MO) under visible light (80 mW·cm⁻², 150 min) that were 17.9 and 1.4 times higher than those of the pure In₂O₃ and ZnIn₂S₄, respectively. Moreover, the 40In₂O₃/ZnIn₂S₄ exhibited an obviously improved antibacterial performance against Pseudomonas aeruginosa, with an antibacterial rate of 99.8% after visible light irradiation of 80 mW cm⁻² for 420 min. The 40In₂O₃/ZnIn₂S₄ composite showed the highest photocurrent density, indicating an enhanced separation of photogenerated charge carriers. Electron spin resonance results indicated that the 40In₂O₃/ZnIn₂S₄ composite generated both ·O₂⁻ and ·OH radicals under visible light, whereas ·OH radicals were almost not detected in ZnIn₂S₄ alone, suggesting the presence of a Z-scheme heterojunction between In₂O₃ and ZnIn₂S₄, thereby enhancing the degradation and antibacterial capabilities of the composite. This offers fresh perspectives on designing effective photocatalytic materials for use in antibacterial and antifouling applications.

In this study, Bi₂MoO₆ nanoflowers with different molybdenum sources were in situ grown on the surface of g-C₃N₄ nanosheets (OCN) by a simple one-step solvothermal method. The effects of doping and different molybdenum sources on the photocatalytic degradation and bactericidal activity of Bi₂MoO₆/OCN were discussed. Among them, the solvothermal preparation of P-Bi₂MoO₆/OCN using phosphomolybdic acid as molybdenum source can make up for the shortcomings caused by the destruction of OCN structure by generating more lattice defects to promote charge separation and constructing Lewis acid/base sites to effectively improve the photocatalytic performance. In addition, by adding phosphoric acid to increase the P-doped content, more exposed alkaline active sites are induced on the surface of P-Bi₂MoO₆/OCN, as well as larger specific surface area and charge transfer efficiency, which further improve the photocatalytic performance. Finally, the optimized 16P-Bi₂MoO₆/OCN showed a degradation rate of 99.7% for 20 mg/L rhodamine B (RhB) within 80 min under visible light, and the antibacterial rates against E. coli, S. aureus and P. aeruginosa within 300 min were 99.58%, 98.20% and 97.48%, respectively. This study provides a reference for optimizing the synthesis of environmentally friendly, solar-responsive, photocatalytic sterilization materials from the perspective of preparation, raw materials and structure.

Juglone (5-hydroxy-1,4-naphthalenedione), a natural compound derived from walnut husks, was investigated as a sustainable dual-function antibacterial agent and corrosion inhibitor for Q235 steel in sulfate-reducing bacteria (SRB)-containing seawater. Juglone was synthesized via an improved one-pot method, and its performance was evaluated through antibacterial assays, weight loss measurements, surface characterization (SEM, XPS, XRD), and electrochemical techniques (EIS, PDP). Juglone exhibited potent antibacterial activity against Desulfovibrio sp., with a minimum inhibitory concentration (MIC) of 40 mg/L. At 20 mg/L (0.5 MIC) and 40 mg/L (1 MIC), it effectively suppressed bacterial growth and metabolism, mitigating corrosion. At 80 mg/L (2 MIC), a dual-action mechanism was observed: strong antibacterial effect combined with chemical reaction with H₂S, a corrosive SRB metabolite, forming a protective thiol-containing film on the steel surface. This reduced the corrosion current density from 3.16 × 10⁻⁵ A/cm² to 7.94 × 10⁻⁷ A/cm², achieving an inhibition efficiency of 97.5%. Juglone represents a promising green alternative to conventional toxic antibacterial agents, aligning with circular economy principles.