Platinum–carbon catalysts are widely used in the manufacturing of proton-exchange membrane fuel cells. Increasing Pt/C activity and stability is an urgent task and the optimization of their structure seems to be one of the possible solutions. In the present paper, Pt/C electrocatalysts containing small (2–2.6 nm) nanoparticles (NPs) of a similar size, uniformly distributed over the surface of a carbon support, were obtained by the original method of liquid-phase synthesis. A comparative study of the structural characteristics, catalytic activity in the oxygen electroreduction reaction (ORR), and durability of the synthesized catalysts, as well as their commercial analogs, was carried out. It was shown that the uniformity of the structural and morphological characteristics of Pt/C catalysts makes it possible to reduce the negative effect of the small size of NPs on their stability. As a result, the obtained catalysts were significantly superior to their commercial analogs regarding ORR activity, but not inferior to them in terms of stability.

Thin nanocrystalline transparent Al-doped ZnO (1–10 at.% Al) films were synthesized by solid-phase pyrolysis at 700 °C. Synthesized Al-doped ZnO films were investigated by X-ray diffraction (XRD), scanning and transmission electron microscopy (SEM, TEM). All obtained materials were crystallized into the wurtzite structure, which was confirmed by XRD. The material crystallinity decreases with the introduction of aluminum. SEM and TEM showed that the films are continuous and have a uniform distribution of nanoparticles with an average size of 15–20 nm. TEM confirmed the production of Al-doped ZnO films. The transmittance of Al-doped ZnO films in the range of 400–1000 nm is more than 94%. The introduction of 1% Al into ZnO leads to a narrowing of the band gap compared to ZnO to a minimum value of 3.26 eV and a sharp decrease in the response time to the radiation exposure with a wavelength of 400 nm. An increase in aluminum concentration leads to a slight increase in the band gap, which is associated with the Burstein–Moss effect. The minimum response time (8 s) was shown for film containing 10% Al, which is explained by the shortest average lifetime of charge carriers (4 s).