Recently, nanomaterials have attracted attention in the field of pavement construction as modifiers to endure heavy loads and climate changes. In this study, conventional asphalt (bitumen) of penetration grade AC (60/70) was modified with graphene platelets (GnPs) at three different contents: 0.5%, 1.0%, and 1.5% by weight of asphalt content. Kinematic viscosity, softening point, penetration, and dynamic shear rheology tests were performed to evaluate the mechanical properties of modified binder. The results showed that adding GnPs improves the mechanical properties of asphalt binder; the kinematic viscosities, softening points, and rutting parameters increased but penetrations decreased with the contents of GnPs. Hot mix asphalt specimens with GnPs-modified asphalt were prepared and characterized with Marshall tests, thermal stress restrained specimen tests (TSRST), wheel tracking tests, and indirect tensile tests. Similar to the results of asphalt binder, the mechanical properties of asphalt mixture were improved by GnPs. Marshall stability increased by 21% and flow decreased by 24% with accepted value of 2.8 mm in penetration when the mixture was modified with 1.0 wt% of GnPs. At the same GnPs content, modified asphalt mixture led to lower failure temperature by 2 °C in comparison with unmodified asphalt mixture and the cryogenic failure stress was improved by 12%. The wheel tracking tests showed that GnPs-modified asphalt mixture has outstanding deformation resistance in comparison with unmodified asphalt mixtures: after 5000 cycles, 1.0 wt% of GnPs reduced the rut depth of asphalt mixture by 60%—the rut depth of unmodified asphalt mixture was 6.9 mm compared to 2.75 mm for modified asphalt mixture. After 10,000 cycles, the modified asphalt mixture showed rut depth of 3.24 mm in comparison with 8.12 mm in case of unmodified asphalt mixture. Addition of GnPs into asphalt mixture significantly improved the indirect tensile strength: 1.0 wt% of GnPs increased the indirect tensile strength of unmodified asphalt mixture from 0.79 to 1.1 MPa recording ~40% increment. The results of this study can confirm that graphene platelets enhance the mechanical properties of asphalt mixture and its performance.

Weak subgrade is the main problem facing most highway projects. Therefore, this study focuses on trying to improve the properties and increase the strength of weak, clayey, swelling soil for use as a subgrade for pavement structural sections. This trial was developed using a mix of granular and chemical stabilization for the soil. Granular stabilization was applied firstly by mixing natural sand at different percentages of 20%, 35%, and 50% of the total weight of clayey, swelling soil samples to find the minimum percentage that could be added to improve it to sandy, clayey soil, which is acceptable as a subgrade according to the Egyptian highway specification code. Secondly, chemical stabilization was applied to enhanced sandy, clayey soil to increase its strength properties. This was performed by adding chemical additives (lime, cement kiln dust (CKD), fiberglass, Addicrete 11, and gypsum) at different ratios of 2%, 4%, and 6% of the total weight of the samples of enhanced sandy, clayey soil. An experimental program was conducted consisting of characteristics and consistency tests, the California bearing ratio (CBR) test, a proctor test, and a consolidated-drained (C-D) tri-axial shear test. The results showed that 50% sand was the minimum percentage that could be mixed with swelling, clayey soil for granular stabilization to be enhanced and become sandy, clayey soil, which is accepted as a subgrade layer according to the Egyptian highway specification code. In addition, using a mix of granular and chemical stabilization increased the compressive strength of this enhanced subgrade by adding 6% lime or cement kiln dust (CKD) of the total sample weight. They enhanced the strength of the soil and reduced its plasticity. Adding 6% fiberglass and polymers could slightly enhance the desired properties; however, it is not recommended to use them due to their slight effect and economic cost. In addition, it is not recommended to use gypsum at more than 4% due to its negative effect on CBR.