The study of powder metallurgy processing methods for titanium represents a promising avenue that can respond to a growing demand. This work reports the feasibility of direct powder forging (DPF) as a method to process large spherical Ti-6Al-4V powder into wrought products with noteworthy properties and physical characteristics. Direct powder forging is a thermomechanical process that imparts uniaxial loading to an enclosed and uncompacted powder to produce parts of various sizes and shapes. Stainless steel canisters were filled with prealloyed Ti-6Al-4V powder and consolidated through a multi-step open-die forging and rolling process into wrought DPF bars. After DPF, annealing was performed in the upper α+β phase. The results show that full consolidation was achieved and higher mechanical properties than the Ti-6Al-4V grade F-23 requirements in annealed conditions were obtained. The results also show that direct powder forging of spherical titanium powder could produce wrought mill products and exhibit some potential for further investigation for industrial applications.

This study investigates direct powder forging (DPF) as a new approach for near-net-shape processing of titanium alloys using a coarse particle size distribution (PSD) between 90 and 250 μm. This route was utilised to takes advantage of DPF’s enclosed nature to make near-net-shape components with conventional forging equipment, making it attractive and viable even for reactive powder such as titanium. In this study, the uncompacted Ti-6Al-4V ELI powder was sealed under vacuum in a stainless-steel canister and hot forged in air to produce a fully dense titanium femoral stem. After the final forging stage, the excess material in the flash region was cut, which efficiently released the canister, revealing the forged part with minimal surface contamination. The as-forged microstructure comprises coarse β grains with a martensitic structure. The subsequent annealing was able to generate a fine and homogenous lamellar microstructure with mechanical properties that respects the surgical implant standard, showing that DPF offers significant potential for forged titanium parts. Therefore, the DPF process provides a suitable alternative to produce titanium components using basic equipment, making it more available to the industry.