Ionically, cross-linked alginate gels have a potential to be used in a wide range of biomedical, environmental and catalytic applications. The study deals with preparation of alginate hydrogels cross-linked with various cations and the analysis of their equilibrium swelling and mechanical properties. It is shown that the type of cations used in the cross-linking process affects the elastic moduli and the equilibrium degree of swelling of the gels. The experimental data in small-amplitude oscillatory tests are fitted with a model that involves two material parameters: the elastic modulus of a polymer network and a measure of its inhomogeneity. The influence of cations on these quantities is studied numerically. It is revealed that the dependence of the elastic modulus of ionically cross-linked alginate gels on their equilibrium degree of swelling differs from that predicted by the conventional theory for covalently cross-linked gels.

A new two-step method is suggested for the preparation of homogeneous alginate gels. In the first step, alginate chains are weakly bonded by Ca${}^{2+}$ ions in an aqueous solution with a low pH. In the next step, the gel is immersed into a strong solution of CaCl${}_2$ to finalize the cross-linking process. Homogeneous alginate gels preserve their integrity in aqueous solutions with a pH ranging from 2 to 7 and ionic strength in the interval from 0 to 0.2 M, at temperatures ranging from room temperature up to 50 °C, and can be used in biomedical applications. The immersion of these gels into aqueous solutions with low pH induces the partial breakage of ionic bonds between chains (treated as gel degradation). This degradation affects the equilibrium and transient swelling of homogeneous alginate gels and makes them sensitive to the history of loading and environmental conditions (pH, ionic strength and temperature of aqueous solutions). As sensitivity to the environmental stimuli is a characteristic feature of polymer networks connected by catch bonds, homogeneous alginate gels may serve as a simple model, mimicking the behavior of more sophisticated structures in living matter.