In many cases, service life of reinforced concrete structures is severely limited by chloride penetration until the steel reinforcement or by carbonation of the covercrete. Water repellent treatment on the surfaces of cement-based materials has often been considered to protect concrete from these deteriorations. In this paper, three types of water repellent agents have been applied on the surface of concrete specimens. Penetration profiles of silicon resin in treated concrete have been determined by FT-IR spectroscopy. Water capillary suction, chloride penetration, carbonation, and reinforcement corrosion in both surface impregnated and untreated specimens have been measured. Results indicate that surface impregnation reduced the coefficient of capillary suction of concrete substantially. An efficient chloride barrier can be established by deep impregnation. Water repellent surface impregnation by silanes also can make the process of carbonation action slow. In addition, it also has been concluded that surface impregnation can provide effective corrosion protection to reinforcing steel in concrete with migrating chloride. The improvement of durability and extension of service life for reinforced concrete structures, therefore, can be expected through the applications of appropriate water repellent surface impregnation.

Water repellent treatment has been considered an effective preventive method against water and aggressive ions penetration into concrete and consequently can improve the durability of concrete structures. In reality, many concrete structures are exposed to conditions with high risk of carbonation. In this contribution, one type of ordinary concrete had been prepared and surface impregnated by 400 g/m²silane cream and 100 g/m²and 400 g/m²silane gel. In addition, integral water repellent concrete was produced by adding 2% silane emulsion. Then, the specimens were exposed to accelerated carbonation for 7, 28, and 72 days. The effect of water repellent treatment on carbonation of concrete has been investigated. The results indicate that surface impregnation reduced carbonation depth of concrete under RH 70%, but integral water repellent concrete increased carbonation. Carbonation reaction started behind the hydrophobic layer in the surface-impregnated concrete. The coefficient of carbonation can be described better by a hyperbolic function of time. Treatment by 400 g/m²silane gel and silane cream showed better efficiency on reducing carbonation than usage of 100 g/m². Coefficient of water capillary suction was decreased significantly by both surface impregnation and integral water repellent treatment. It is an effective method to protect concrete from water penetration into the material.

The experiment study on the air-entrained concrete of 100 mm cubes under triaxial compression with different intermediate stress ratioα2=σ2D : σ3Dwas carried out using a hydraulic-servo testing system. The influence of rapid freeze-thaw cycles and intermediate stress ratio on the triaxial compressive strengthσ3Dwas analyzed according to the experimental results, respectively. The experimental results of air-entrained concrete obtained from the study in this paper and the triaxial compression experimental results of plain concrete got through the same triaxial-testing-system were compared and analyzed. The conclusion was that the triaxial compressive strength is greater than the biaxial and uniaxial compressive strength after the same rapid freeze-thaw cycles, and the increased percentage of triaxial compressive strength over biaxial compressive strength or uniaxial compressive strength is dependent on the middle stress. The experimental data is useful for precise analysis of concrete member or concrete structure under the action complex stress state.

This study investigates the enhancement of hydraulic lime mortar (HLM) using varying contents of metakaolin (MK) to improve its application in the restoration of historic buildings. Samples from historic structures were analyzed, and the effects of different MK contents on the physical and mechanical properties of HLM were examined. The reaction mechanism and microstructural changes were evaluated using XRD and SEM analysis. The results indicated that increasing MK levels in HLM led to a decrease in fluidity, with fluidity reducing by 4.8% at 12% MK. The addition of MK increased water consumption for standard consistency by 5.4% and shortened the final setting time by 10.2%. MK consumption promoted secondary hydration, enhancing compressive strength by up to 98.1% and flexural strength by up to 55.1%, and increasing bonding strength by 26.9%. The density of HLM improved with MK addition, slightly reducing moisture content by 4.5% and water absorption by 4.6%, while the water vapor transmission properties decreased by 50.9%, indicating reduced porosity. The elastic modulus of the mortar increased significantly from 2.19 GPa to 7.88 GPa with the addition of MK, enhancing rigidity and crack resistance. The optimal blend for restoration materials was found to be 9.0% MK and 25.0% heavy calcium carbonate and was characterized by moderate mechanical strength, enhanced early strength, commendable permeability, minimal risk of cracking, and ease of application. This blend is highly suitable for the rehabilitation of historic structures.