Effects of scanning strategy during powder bed fusion electron beam additive manufacturing (PBF-EB AM) on microstructure, nano-mechanical properties, and creep behavior of Ti6Al4V alloys were compared. Results show that PBF-EB AM Ti6Al4V alloy with linear scanning without rotation strategy was composed of 96.9% α-Ti and 2.7% β-Ti, and has a nanoindentation range of 4.11–6.31 GPa with the strain rate ranging from 0.001 to 1 s⁻¹, and possesses a strain-rate sensitivity exponent of 0.053 ± 0.014. While PBF-EB AM Ti6Al4V alloy with linear and 90° rotate scanning strategy was composed of 98.1% α-Ti and 1.9% β-Ti and has a nanoindentation range of 3.98–5.52 GPa with the strain rate ranging from 0.001 to 1 s⁻¹, and possesses a strain-rate sensitivity exponent of 0.047 ± 0.009. The nanohardness increased with increasing strain rate, and creep displacement increased with the increasing maximum holding loads. The creep behavior was mainly dominated by dislocation motion during deformation induced by the indenter. The PBF-EB AM Ti6Al4V alloy with only the linear scanning strategy has a higher nanohardness and better creep resistance properties than the alloy with linear scanning and 90° rotation strategy. These results could contribute to understanding the creep behavior of Ti6Al4V alloy and are significant for PBF-EB AM of Ti6Al4V and other alloys.

This study elucidates the influence of rapid heating (300 °C/s) on martensitic transformation pathways, crystallographic variant selection, and the resulting mechanical performance in a medium-carbon steel. Compared with conventional heating, rapid heating markedly refines the prior austenite grain (PAG) and martensitic substructures, reducing the mean PAG size from 16.08 μm to 5.06 μm and the martensitic block size from 4.24 μm to 2.41 μm. The accelerated austenitizing and quenching promote a higher density of high-angle grain boundaries (HAGBs) and favor variant selection dominated by the closely packed (CP) group. Σ3 twin boundaries are also found to assist variant nucleation and contribute to microstructural complexity. Despite a marginal decrease in tensile strength, rapid-heated steels exhibit significantly enhanced ductility and a 28.3% increase in the product of strength and elongation (PSE) compared to their conventionally treated counterparts. These findings demonstrate that rapid heating not only enables effective refinement of martensitic substructures but also offers a powerful means of controlling variant evolution, thereby achieving a superior strength–ductility synergy in martensitic steels.