Hybrid organic–inorganic perovskites providing integrated functionalities for multimodal switching applications are widely sought-after materials for optoelectronics. Here, we embark on a study of a novel pyrrolidinium-based cyanide perovskite of formula (C₄H₁₀N)₂KCr(CN)₆, which displays thermally driven bimodal switching characteristics associated with an order–disorder phase transition. Dielectric switching combines two features important from an application standpoint: high permittivity contrast (Δε′ = 38.5) and very low dielectric losses. Third-order nonlinear optical switching takes advantage of third-harmonic generation (THG) bistability, thus far unprecedented for perovskites and coordination polymers. Structurally, (C₄H₁₀N)₂KCr(CN)₆ stands out as the first example of a three-dimensional stable perovskite among formate-, azide-, and cyanide-based metal–organic frameworks comprising large pyrrolidinium cations. Its stability, reflected also in robust switching characteristics, has been tracked down to the Cr³⁺ component, the ionic radius of which provides a large enough metal–cyanide cage for the pyrrolidinium cargo. While the presence of polar pyrrolidinium cations leads to excellent switchable dielectric properties, the presence of Cr³⁺ is also responsible for efficient phosphorescence, which is remarkably shifted to the near-infrared region (770 to 880 nm). The presence of Cr³⁺ was also found indispensable to the THG switching functionality. It is also found that a closely related cobalt-based analogue doped with Cr³⁺ ions displays distinct near-infrared phosphorescence as well. Thus, doping with Cr³⁺ ions is an effective strategy to introduce phosphorescence as an additional functional property into the family of cobalt-cyanide thermally switchable dielectrics.

A series of five alcohols (3-methyl-2-butanol, 1-cyclopropylethanol, 1-cyclopentylethanol, 1-cyclohexylethanol, and 1-phenylethanol) was used to study the impact of the size of steric hindrance and its aromaticity on self-assembling phenomena in the liquid phase. In this Letter, we have explicitly shown that the phenyl ring exerts a much stronger effect on the self-organization of molecules via the O–H···O scheme than any other type of steric hindrance, leading to a significant decline in the size and concentration of the H-bonded clusters. Given the combination of calorimetric, dielectric, infrared, and diffraction studies, this phenomenon was ascribed to its additional proton-acceptor function for the competitive intermolecular O–H···π interactions. The consequence of this is a different packing of molecules on the short- and medium-range scale.

In metal halide perovskites, the complex dielectric screening together with low energy of phonon modes leads to non-negligible Fröhlich coupling. While this feature of perovskites has already been used to explain some of the puzzling aspects of carrier transport in these materials, the possible impact of polaronic effects on the optical response, especially excitonic properties, is much less explored. Here, with the use of magneto-optical spectroscopy, we revealed the non-hydrogenic character of the excitons in metal halide perovskites, resulting from the pronounced Fröhlich coupling. Our results can be well described by the polaronic-exciton picture where electron and hole interactions are no longer described by a Coulomb potential. Furthermore, we show experimental evidence that the carrier-phonon interaction leads to the enhancement of the carrier's effective mass. Notably, our measurements reveal a pronounced temperature dependence of the carrier's effective mass, which we attribute to a band structure renormalization induced by the population of low-energy phonon modes. This interpretation finds support in our first-principles calculations.

Comprehensive investigations revealed a pressure–temperature phase diagram for 2D hybrid perovskite MHy₂PbI₄, demonstrating its high structural elasticity and ability to generate polar phases mimicking its ferroelectric analogue MHy₂PbBr₄.

Three-dimensional organic-inorganic perovskites are rapidly evolving materials with diverse applications. This study focuses on their two representatives - acetamidinium manganese(II) formate (AceMn) and formamidinium manganese(II) formate (FMDMn) – subjected to varying temperature and pressure. We show that AceMn undergoes atypical pressure-induced structural transformations at room temperature, increasing the symmetry from ambient-pressure P2₁/n phase II to the high-pressure Pbca phase III. In turn, FMDMn in its C2/c phase II displays temperature- and pressure-induced ordering of cage cations that proceeds without changing the phase symmetry or energy barriers. The FMD⁺ cations do not order under constant volume across the pressure-temperature plane, despite similar pressure and temperature evolution of the unit-cell parameters. Temperature and pressure affect the cage cations differently, which is particularly pronounced in their relaxation dynamics seen by dielectric spectroscopy. Their motion require a rearrangement of the metal-formate framework, resulting in the energy and volumetric barriers defined by temperature-independent activation energy and activation volume parameters. As this process is phonon-assisted, the relaxation time is strongly temperature-dependent. Consequently, relaxation times do not scale with unit-cell volume nor H-bond lengths in formates, offering the possibility of tuning their electronic properties by external stimuli (like temperature or pressure) even without any structural changes.