The application of recycled coarse aggregate (RCA) made from waste concrete to replace natural coarse aggregate (NCA) in concrete structures can essentially reduce the excessive consumption of natural resources and environmental pollution. Similar to normal concrete structures, recycled concrete structures would also suffer from the damage of carbonation, which leads to the deterioration of durability and the reduction of service life. This paper presents the experimental results of the cubic compressive strength, the static elastic modulus and the stress–strain relation of recycled coarse aggregate concrete (RAC) after carbonation. The results show that the cubic compressive strength and the static elastic modulus of carbonated RAC gradually increased with the carbonation depth. The uncarbonated and fully carbonated RAC show smaller static elastic modulus than natural aggregate concrete (NAC). As the carbonation depth increased, the peak stress increased, while the peak strain decreased and the descending part of the curves gradually became steeper. As the content of RCA became larger, the peak stress decreased, while the peak strain increased and the descending part of the curves gradually became steeper. An equation for stress–strain curves of RAC after carbonation was proposed, and it was in good agreement with the test results.

To improve the safety of orthotropic steel bridge decks and the construction efficiency of bridge deck pavement by enhancing the performance of pavement materials, a new-generation, high-performance cold-mix resin was prepared by carrying out the combination of micro-characteristic analysis and performance test. Meanwhile, the pavement performance and fatigue performance of high-performance cold-mix resin mixtures and hot-mix epoxy saphalt mixtures as a control group were studied experimentally. The results show that different kinds of epoxy resins show bisphenol structure in essence. The curing exothermic peak temperature of the cold-mix resin increases with the heating rate. Both the specific heat capacity (△C_P) of cold-mix resin and cold-mix resin asphalts exhibit a sudden change between −20 °C and 40 °C. In resin asphalt mixtures, cold-mix resin forms the network structure skeleton whereas the asphalt distributed in the form of tiny particles. The dosage of respective component has a significant effect on the tensile strength and elongation at break of cold-mix resin. Compared with hot-mix epoxy asphalt mixtures, cold-mix resin mixtures exhibit comparable water stability and high and low-temperature performance, as well as greater fatigue life.

This paper experimentally investigated the effects of varying contents of Na₂O in a modified sodium silicate, sodium silicate moduli (M_s), and contents of granulated blast furnace slag (GBFS) on the compressive strength and drying shrinkage of fly ash (FA)-based geopolymer grouting materials at different ages. X-ray diffraction (XRD), mercury intrusion porosimetry (MIP), and scanning electron microscopy–energy dispersive X-ray spectroscopy (SEM–EDS) were used to study the influences of different amounts of GBFS on the microstructure and product compositions of FA-based geopolymer grouting materials. The results show that the content of Na₂O in modified sodium silicate, M_s, and the content of GBFS play a significant role in compressive strength and drying shrinkage of FA-based geopolymer grouting materials. In addition, the influence of M_s as well as the content of GBFS on the compressive strength and drying shrinkage of FA-based geopolymer grouting materials was deeply affected by curing age. The micro-performance tests and analysis clearly showed that incorporating 30 wt% GBFS can decrease the proportion of pores with large pore sizes, improve pore size distribution, and enhance the solubility of FA and further promote the formation of C-A-S-H gel within FA-based geopolymer grouting materials.