This paper seeks to examine how the Mn–Co spinel interconnect coating microstructure can influence Cr contamination in an oxygen electrode of intermediate temperature solid oxide cells, at an operating temperature of 750 °C. A Mn–Co spinel coating is processed on Crofer 22 APU substrates by electrophoretic deposition, and subsequently sintered, following both the one-step and two-step sintering, in order to obtain significantly different densification levels. The electrochemical characterization is performed on anode-supported cells with an LSCF cathode. The cells were aged prior to the electrochemical characterization in contact with the spinel-coated Crofer 22 APU at 750 °C for 250 h. Current–voltage and impedance spectra of the cells were measured after the exposure with the interconnect. Post-mortem analysis of the interconnect and the cell was carried out, in order to assess the Cr retention capability of coatings with different microstructures.

This study presents results on the development of strontium oxide (SrO) containing glass sealants used to join Crofer22APU to yttria-stabilized zirconia (3YSZ), in which the main glass components, that is, silicon oxide (SiO₂), strontium oxide (SrO), calcium oxide (CaO) and aluminum oxide (Al₂O₃), have been varied appropriately. Certain properties, such as the crystallization behavior, the coefficient of thermal expansion, adhesion, and reactivity of the sealants in contact with Crofer22APU, have been reviewed and discussed. The optimized glass composition (with CTE in the 9.8–10.3 × 10⁻⁶ K⁻¹ range) results in a good joining behavior by hindering the formation of undesirable strontium chromate (SrCrO₄) on contact with the Crofer22APU steel after 1000 h. at 850 °C. High specific resistivity values of about 10⁶ Ohm.cm have been obtained, thus demonstrating good insulating properties at 850 °C under an applied voltage of 1.6 V. A negligible degradation in the electrical resistivity trend was measured during the test up to 1000 h, thus excluding the presence of detrimental reactions of the glass-ceramic sealant in contact with Crofer22APU under a dual atmosphere, as confirmed using SEM-EDS post-mortem analyses.