The effect of cylinder liners on engine performance is substantial. Typically, the cylinder surfaces were plateau honed. However, recently additional dimples or grooves were created on them. This work discusses the tribological impacts of textured cylinder liner surfaces based on a review of the literature. The results of the experimental research obtained using test rigs and fired engines were critically reviewed. In addition, the results of the modeling are shown. Circular oil pockets and grooves perpendicular to the sliding direction of piston rings of small depths were typically used. Surface texturing of the cylinder liners governs lubrication between the cylinder liner and the piston ring by an increase in oil film thickness near the reversal points leading to reductions in friction force and wear and in the fired engine to a decrease in fuel consumption and to an increase in power or torque. The correct texturing pattern ensures a decrease in the oil consumption, blow-by, and emissions of the internal combustion engine compared to plateau-honed surfaces. Considerations of future challenges are also addressed. The volume of lubricant reservoir in surface topography, called oil capacity, should be a substantial parameter characterizing textured surfaces.

Surface texturing is an option of surface engineering resulting in reduction of friction due to the creation of isolated dimples or grooves on sliding surfaces. The purpose of this work is to find the effect of the groove bottom profiles on the reduction of the friction force. Investigations were conducted using an Optimol SRV5 tribotester equipped with a pin-on-disc module. A disc made of 42CrMo4 steel, with a 100 mm diameter acted as a sample. A counter-sample was made of the same material, however, its diameter was 20 mm. The sliding conditions were selected to be similar to those of a sliding crankpin bearing pad operating in a high-performance internal combustion engine. Surface texturing was found to be beneficial for a reduction in the friction coefficient up to 55% in comparison to the untextured disc. Tribological performances of discs with spiral groove patterns were better than those with a radial layout. In most cases the convergent profile of the groove bottom was superior to the dam shape.

The constant development of environmental protection causes the necessity to increase the efficiency of machines. By increasing the efficiency of machines, energy losses can be limited, leading to lower energy consumption. Friction reduction leads to an increase in efficiency and a decrease in wear. In this paper, selected surface texturing methods, such as burnishing and abrasive jet machining, with their limitations are presented. Thanks to those processes, various surface textures can be obtained. Examples of applications of these methods for friction and wear reduction are shown.

The experiment was carried out in a reciprocating lubricated conformal sliding contact between steel discs of the same hardness. The effects of disc surface texturing on the friction coefficient at various operating conditions (temperature, normal load, and frequency of oscillations) were studied. Under various conditions, surface texturing caused friction reductions of sliding pairs. The largest reduction was 4.6 times at a lower temperature and 2.5 times at a higher temperature. The effect of the pit area ratio on the friction reduction was visible at a higher temperature. The highest dimple density of 25% corresponded to a lower coefficient of friction than the smallest density of 9%. The sliding pair with a dimple density of 17% led to large variation of the friction force. At lower temperatures, the coefficients of friction were lower compared to tests at higher temperatures.

Surface texturing is designed to improve the functional properties of machine elements by generating dimples on the surface contacted. Friction and wear resistance can also be improved by creating diamond-like carbon (DLC) coatings. These two techniques were combined to extend the lifetime of the elements and minimise friction in reciprocating conformal sliding contact. This work is functionally important for assemblies operating under high normal loads. Experiments were carried out in initially lubricated reciprocating sliding contact using an Optimol SRV 5 tribotester in the flat-on-flat configuration. The disc samples were untextured, laser textured, and DLC-coated untextured and textured. The combination of DLC coating and surface texturing caused an enhancement of the tribological performance of the sliding pair compared to that of untextured discs with and without DLC coating and textured discs without DLC coating. The DLC coating of the untextured disc caused a growth in the lifetime of a friction pair by a factor of 2.4. Seizure resistance also increased due to surface texturing of the steel disc for pit area ratios of 9 and 13%. Combining surface texturing with pit area ratios of 3 and 9% and DLC coating led to a decrease in the coefficients of friction of sliding pairs compared to only textured and coated discs. The DLC coating caused a decrease in the wear of the disc sample and reduction in wear levels of the counter samples in comparison to those of textured discs without DLC coatings.

During co-action between contact elements in reciprocating motion, different working conditions exist in outer and inner zones of stationary elements. Because the tribological effects of surface texturing depend on the operating conditions, various dimple patterns were created in the middle part of the steel disc and near the reversal points. The behaviors of variable dimple patterns were compared with those of uniform texturing and untexturing. It was found that the dimple patterns in the middle disc zone depended on the resistance to motion. The best tribological behavior was obtained for a pit area ratio of 13% and diameter of 0.4 mm in the inner zone, and pit area ratio of 3% and diameter of 0.2 mm in the outer zones. Low resistance to motion and the smallest friction variation of all tested sliding pairs were achieved. For the same pit area ratio of 13% in a disc of 0.4 mm, the dimple diameter behaved better than in the 0.2 mm diameter disc. The greatest decrease in the coefficient of friction of 85% compared to untextured sliding pair was achieved for uniform laser texturing with a pit area ratio of 13% and dimple diameter of 0.4 mm, when the normal load was 40 N and frequency of displacement was 20 Hz.