Fused filament fabrication (FFF), as a form of additive manufacturing (AM), in recent years, has become a popular method to manufacture prototypes, as well as functional parts. FFF is an extrusion process, commonly known as 3D printing, where the object is built by depositing melted material layer by layer. The most common materials, i.e., the materials that are most widely used, are polylactic acid (PLA), acrylonitrile butadiene styrene (ABS) and acrylonitrile styrene acrylate (ASA). Although there are lot of research papers that cover the subject of the determination of mechanical properties and characteristics, theoretically and experimentally, as well as the fatigue characteristics of aforementioned materials, there is a lack of research and scientific papers dealing with the problematics of S–N curves based on the rotating bending fatigue analysis of those materials. Consequently, this paper covers the topic of rotating bending fatigue data for 3D printed specimens of given materials, under different loading values.

The correct choice of a material in the process of structural design is the most important task. This study deals with determining and analyzing the mechanical properties of the material, and the material resistance to short-time creep and fatigue. The material under consideration in this investigation is austenitic stainless steel X6CrNiTi18-10. The results presenting ultimate tensile strength and 0.2 offset yield strength at room and elevated temperatures are displayed in the form of engineering stress-strain diagrams. Besides, the creep behavior of the steel is presented in the form of creep curves. The material is consequently considered to be creep resistant at temperatures of 400 °C and 500 °C when subjected to a stress which is less than 0.9 of the yield strength at the mentioned temperatures. Even when the applied stress at a temperature of 600 °C is less than 0.5 of the yield strength, the steel may be considered as resistant to creep. Cyclic tensile fatigue tests were carried out at stress ratio R = 0.25 using a servo-pulser machine and the results were recorded. The analysis shows that the stress level of 434.33 MPa can be adopted as a fatigue limit. The impact energy was also determined and the fracture toughness assessed.

This paper considers the applicability of virtual crack closure technique (VCCT) for calculation of stress intensity factor range for crack propagation in standard metal specimen geometries with sharp through thickness cracks. To determine crack propagation rate and fatigue lifetime of a dynamically loaded metallic specimen, in addition to VCCT, standard Forman model was used. Values of stress intensity factor (SIF) ranges ΔK for various crack lengths were calculated by VCCT and used in conjunction with material parameters available from several research papers. VCCT was chosen as a method of choice for the calculation of stress intensity factor of a crack as it is simple and relatively straightforward to implement. It is relatively easy for implementation on top of any finite element (FE) code and it does not require the use of any special finite elements. It is usually utilized for fracture analysis of brittle materials when plastic dissipation is negligible, i.e., plastic dissipation belongs to small-scale yielding due to low load on a structural element. Obtained results showed that the application of VCCT yields good results. Results for crack propagation rate and total lifetime for three test cases were compared to available experimental data and showed satisfactory correlation.

The article deals with the analysis of the mechanical behavior at different temperatures, uniaxial creep and uniaxial fatigue of martensitic steel X46Cr13 (1.4034, AISI 420). For the purpose of considering the aforementioned mechanical behavior, as well as determining the appropriate resistance to creep and fatigue strength levels, numerous uniaxial tests were carried out. Tests related to mechanical properties performed at different temperatures are presented in the form of engineering stress-strain diagrams. Short-time creep tests performed at different temperatures and different stress levels are presented in the form of creep curves. Fatigue tests carried out at stress ratios $R=0.25$ and $R=-1$ are shown in the form of S–N (fatigue) diagrams. The finite fatigue regime for each of the mentioned stress ratios is modeled by an inclined log line, while the infinite fatigue regime is modeled by a horizontal line, which represents the fatigue limit of the material and previously was calculated by the modified staircase method. Finally, the fracture toughness has been calculated based on the Charpy V-notch impact energy.