The Si nanograss arrays are directly grown on Si substrate via catalyst-assisted VLS growth and subsequent plasma interaction. AgNPs were rapidly immobilized on Si nanograss arrays for SERS sensing, without any organic reagents and additives.

Corrosion and scaling critically threaten the safety and efficiency of oil–gas gathering stations. Through field inspections, water chemistry analysis, scale characterization, and corrosion simulation in Yanchang oilfield, this study identifies severe localized damage in key components—such as valves, bends, and injection pipelines—with service lives of only 1–2 years. Analysis of over 200 scale samples revealed that CaCO₃ (42 wt%) and CaSO₄ (23 wt%) were the predominant scale types. High salinity >56,000 mg/L, Cl⁻ >31,000 mg/L, and Ca²⁺ promote under-deposit pitting, galvanic corrosion (e.g., Cu–steel couples), and erosion-corrosion at high-velocity zones. Simulations based on OLI Analyzer Studio (a professional thermodynamic simulation software for electrolyte solution and high-salinity brine systems) reveal that the carbon steel (the primary material for the process pipelines and water injection pipelines in the studied oil–gas gathering and transportation stations) has a corrosion rate rising from 0.078 mm/year at 25 °C to 1.94 mm/year at 90 °C. Despite common use of coatings and cathodic protection, these measures often fail to address site-specific failure mechanisms. The study advocates a tailored mitigation strategy combining material compatibility, real-time water monitoring, optimized filtration, and component-level design. This integrated approach enhances asset reliability and operational safety in onshore oilfields.