In this study, we show how strong metal–support interaction (SMSI) oxides in Pt–Nb/SiO₂ and Pt–Ti/SiO₂ affect the electronic, geometric and catalytic properties for propane dehydrogenation. Transmission electron microscopy (TEM), CO chemisorption, and decrease in the catalytic rates per gram Pt confirm that the Pt nanoparticles were partially covered by the SMSI oxides. X-ray absorption near edge structure (XANES), in situ X-ray photoelectron spectroscopy (XPS), and resonant inelastic X-ray scattering (RIXS) showed little change in the energy of Pt valence orbitals upon interaction with SMSI oxides. The catalytic activity per mol of Pt for ethylene hydrogenation and propane dehydrogenation was lower due to fewer exposed Pt sites, while turnover rates were similar. The SMSI oxides, however, significantly increase the propylene selectivity for the latter reaction compared to Pt/SiO₂. In the SMSI catalysts, the higher olefin selectivity is suggested to be due to the smaller exposed Pt ensemble sites, which result in suppression of the alkane hydrogenolysis reaction; while the exposed atoms remain active for dehydrogenation.

Facile synthesis of zero-valent iron nanoparticles has been developed using Tie Guanyin tea extract as reducing and stabilizing agent. The characterization carried out by UV-Vis, SEM, TEM, XRD, and FTIR techniques has identified the successful synthesis of the zero-valent iron nanoparticles. It is evident from the TEM result that spherical zero-valent iron nanoparticles with average size of 6.58±0.76 nm have been obtained through biological method in this study. FTIR spectrum demonstrates that the polyphenols play an important role in the synthetic process. Diffraction peak at 2θ of 44.9° and 49.1° in XRD spectrum explains the existence of the iron nanoparticles. Additionally, effect of concentration of iron nanoparticles and concentration of bromothymol blue on the kinetic rate constants during the degradation process was studied.