In this research, we developed boron-rich nanoparticles that can be used for boron neutron capture therapy as potential carriers for boron delivery to cancerous tissues. Functionalized carbonated boron nitride nanostructures (CBNs) were successfully synthesized in self-propagating combustion waves in mixtures of high-nitrogen explosives and boron compounds. The products’ composition, morphology, and structural features were investigated using Fourier transform infrared spectroscopy, powder X-ray diffraction, low-temperature nitrogen sorption analysis, thermogravimetric analysis, high-resolution scanning electron microscopy, and high-resolution transmission electron microscopy. The extreme conditions prevailing in combustion waves favor the formation of nanosized CBN hollow grains with highly disordered structures that are properly functionalized on the surface and inside the particles. Therefore, they are characterized by high porosity and good dispersibility in water, which are necessary for medical applications. During biological tests, a concentration-dependent effect of the obtained boron nitride preparations on the viability of normal and neoplastic cells was demonstrated. Moreover, the assessment of the degree of binding of fluorescently labeled nanoparticles to selected cells confirmed the relationships between the cell types and the concentration of the preparation at different incubation time points.

Three types of cross-linked porous organic polymers (either oxygen-, nitrogen-, or sulfur-doped) were carbonized under a chlorine atmosphere to obtain chars in the form of microporous heteroatom-doped carbons. The studied organic polymers constitute thermosetting resins obtained via sol-gel polycondensation of resorcinol and five-membered heterocyclic aldehydes (either furan, pyrrole, or thiophene). Carbonization under highly oxidative chlorine (concentrated and diluted Cl₂ atmosphere) was compared with pyrolysis under an inert helium atmosphere. All pyrolyzed samples were additionally annealed under NH₃. The influence of pyrolysis and additional annealing conditions on the carbon materials’ porosity and chemical composition was elucidated.