Promoting metallic magnesium (Mg)-based implants to treat bone diseases in clinics, such as osteosarcoma and bacterial infection, remains a challenging topic. Herein, an iron hydroxide-based composite coating with a two-stage nanosheet-like structure was fabricated on Mg alloy, and this was followed by a thermal reduction treatment to break some of the surface Fe–OH bonds. The coating demonstrated three positive changes in properties due to the defects. First, the removal of –OH made the coating superhydrophobic, and it had self-cleaning and antifouling properties. This is beneficial for keeping the implants clean and for anti-corrosion before implantation into the human body. Furthermore, the superhydrophobicity could be removed by immersing the implant in a 75% ethanol solution, to further facilitate biological action during service. Second, the color of the coating changed from yellow to brown-black, leading to an increase in the light absorption, which resulted in an excellent photothermal effect. Third, the defects increased the Fe²⁺ content in the coating and highly improved peroxidase activity. Thus, the defect coating exhibited synergistic photothermal/chemodynamic therapeutic effects for bacteria and tumors. Moreover, the coating substantially enhanced the anti-corrosion and biocompatibility of the Mg alloys. Therefore, this study offers a novel multi-functional Mg-based implant for osteosarcoma therapy.

We propose a hyperbolic metamaterial-based surface plasmon resonance (HMM-SPR) sensor by composing a few pairs of alternating silver (Ag) and zinc oxide (ZnO) layers. Aiming to achieve the best design for the sensor, the dependence of the sensitivity on the incidence angle, the thickness of the alternating layer and the metal filling fraction are explored comprehensively. We find that the proposed HMM-SPR sensor achieves an average sensitivity of 34,800 nm per refractive index unit (RIU) and a figure of merit (FOM) of 470.7 RIU⁻¹ in the refractive index ranging from 1.33 to 1.34. Both the sensitivity (S) and the FOM show great enhancement when compared to the conventional silver-based SPR sensor (Ag-SPR). The underlying physical reason for the higher performance is analyzed by numerical simulation using the finite element method. The higher sensitivity could be attributed to the enhanced electric field amplitude and the increased penetration depth, which respectively increase the interaction strength and the sensing volume. The proposed HMM-SPR sensor with greatly improved sensitivity and an improved figure of merit is expected to find application in biochemical sensing due to the higher resolution.