The energy absorption in a foam-filled thin-walled circular Al tube was investigated based on the experimentally determined strengthening coefficient of filling using Al and polystyrene closed-cell foams with three different densities. Foam filling was found to change the deformation mode of tube from diamond (empty tube) into concertina, regardless the foam type and density used. Although foam filling resulted in higher energy absorption than the sum of the energy absorptions of the tube alone and foam alone, it was not effective in increasing the specific energy than simply thickening the tube wall. It was shown that for efficient foam filling an appropriate foam-tube combination must be selected by taking into account the magnitude of strengthening coefficient of foam filling and the foam filler plateau load.TÜBİTAK for the Grant # MISAG-22

The effect of rubber, Teflon and aluminum foam interlayer material on the ballistic performance of composite armor was investigated both experimentally and numerically. Although, rubber interlayer did not cause any significant delay in the initial stress build-up in the composite layer, Teflon and aluminum foam interlayer caused a significant delay and reduction in the magnitude of the stress transmitted to the composite backing plate. Damage in the ceramic layer was found to be highly localized around the projectile impact zone for the configuration without interlayer and rubber interlayer while aluminum foam and Teflon interlayer spread the damage zone in the radial direction. Relatively large pieces of the ceramic around the impact axis in the rubber interlayer configuration were observed while the ceramic layer was efficiently fragmented in aluminum foam and Teflon interlayer configuration.TÜBİTAK for the grant # 106M35

The experimental and numerical quasi-static crushing responses of extruded closed cell polystyrene foam-filled thin-walled aluminum tubes were investigated. The numerical crash analysis of empty and foam-filled tubes was performed using the explicit finite element code PAM-CRASH™. Satisfactory agreements were generally achieved between the finite element model and experimental deformed shapes, load–displacements, fold lengths and specific energy absorptions. The model and experiments have also highlighted the several effects of foam filling on the crushing of thin-walled tubes. The energy absorptions in foam-filled tubes were further shown to be higher than the sum of the energy absorptions of empty tube (alone) and filler (alone).TÜBİTAK for the Grant #MISAG-22

In this paper, some of the important defeating mechanisms of the high hardness perforated plates against 7.62 x 54 armor piercing ammunition were investigated. The experimental and numerical results identified three defeating mechanisms effective on perforated armor plates which are the asymmetric forces deviates the bullet from its incident trajectory, the bullet core fracture and the bullet core nose erosion. The initial tests were performed on the monolithic armor plates of 9 and 20 mm thickness to verify the fidelity of the simulation and material model parameters. The stochastic nature of the ballistic tests on perforated armor plates was analyzed based on the bullet impact zone with respect to holes. Various scenarios including without and with bullet failure models were further investigated to determine the mechanisms of the bullet failure. The agreement between numerical and experimental results had significantly increased with including the bullet failure criterion and the bullet nose erosion threshold into the simulation. As shown in results, good agreement between Ls-Dyna simulations and experimental data was achieved and the defeating mechanism of perforated plates was clearly demonstrated