Wood is a hygroscopic material that can reach an equilibrium moisture content when ambient temperature and relative humidity are constant. Moisture affects all properties of wood, as well as its preservative treatment. The hygroscopic behavior of wood can be attributed to the hydroxyl groups of its constituents. Since hemicellulose shows the greatest water affinity, it can be considered the main responsible for the ingress of water into the wood mass. Below the fiber saturation point, wood moisture is only stored in the cell walls. Proton Nuclear Magnetic Resonance (NMR) is a relative method used for the evaluation of moisture content distribution in wood and NMR relaxation is an excellent tool to study the hygroscopic behavior of different woods below the fiber saturation point. This work aimed to test the hypothesis of discriminating among softwoods and hardwoods of different botanical species and identifying further sub-clusters of woods based on the NMR proton spin–spin (T₂) and spin–lattice (T₁) relaxation times of their cell wall water in the hygroscopic moisture range. Importantly, the study was performed using a portable low-cost NMR instrument with which it is possible to investigate wood samples of any size. The main result of this study was that at RH = 94% the relaxation time T_2,2, associated with the cell wall bound water, can be used as a marker to discriminate among softwoods and hardwoods. Graphical abstract

The cleaning of buildings, statues, and artworks composed of stone materials from metal corrosion is an important topic in the cultural heritage field. In this work the cleaning effectiveness of a PVA-PEO-borax hydrogel in removing metal corrosion products from different porosity stones has been assessed by using a multidisciplinary and non-destructive approach based on relaxation times measurement by single-sided portable Nuclear Magnetic Resonance (NMR), Scanning Electron Microscopy—Energy Dispersive Spectroscopy (SEM-EDS), and Raman Spectroscopy. To this end, samples of two lithotypes, Travertine and Carrara marble, have been soiled by triggering acidic corrosion of some copper coins in contact with the stone surface. Then, a PVA-PEO-borax hydrogel was used to clean the stone surface. NMR data were collected in untreated, soiled with corrosion products, and hydrogel-cleaned samples. Raman spectroscopy was performed on PVA-PEO-borax hydrogel before and after cleaning of metal corrosion. Furthermore, the characterization of the dirty gel was obtained by SEM-EDS. The combination of NMR, SEM-EDS and Raman results suggests that the mechanism behind the hydrogel cleaning action is to trap heavy metal corrosion products, such as Cu²⁺ between adjacent boron ions cross-linked with PVA. Moreover, the PVA-PEO-borax hydrogel cleaning effectiveness depends on the stone porosity, being better in Carrara marble compared to Travertine.

In this work, we investigated the potential of PVA-borax hydrogel for cleaning limestones and the dependence of the cleaning on the porosity of the rock and on the action time of the hydrogel treatment. Towards this goal, we used a nuclear magnetic resonance (NMR) spectrometer, developed for non-invasive and non-destructive applications on cultural heritage. T₂-NMR parameters were quantified on different samples of Lecce stone and Travertine cut perpendicular (Pe) and parallel (Pa) to the bedding planes under different experimental conditions: untreated samples, treated with Paraloid B72 and cleaned with PVA-PEO-borax hydrogel applied for 4 min and 2 h. The T₂ results suggest that the effectiveness of the cleaning strongly depended on the porosity of the stones. In Lecce stone, the hydrogel seemed to eliminate both the paramagnetic impurities (in equal measure with 4 min and 2 h treatment) and Paraloid B72. In Travertine Pe, characterized by a smaller pore size compared to Lecce stone, no significant effects were found regarding both the cleaning and the treatment with Paraloid B72. In Travertine Pa, characterized by a larger pore size than the other two samples, the hydrogel seemed to clean the paramagnetic agents (it worked better if applied for a longer time) but it did not appear to have any effect on Paraloid B72 removal.

Currently, one of the most important challenges for the conservation of stone artworks is the removal of metal corrosion products on their surfaces. Traditional cleaning methods, which typically involve the application of aqueous solutions containing chelating agents capable of complexing these metal ions, have shown some weaknesses. These weaknesses become apparent when such methods are applied to statues and other vertical surfaces or when aiming to limit the cleaning process to a specific area with controlled application times. Furthermore, the porosity of the stone surface plays a role concerning the cleaning efficiency. To address these issues, chelating agents can be incorporated into gel-like materials. This study is a proof of concept to evaluate the cleaning efficacy of various gel formulations composed of polyvinyl alcohol (PVA), borax (B), and agarose (AG), loaded with two chelators: ethylenediaminetetraacetic acid (EDTA) and potassium sodium tartrate (PST or Rochelle salt). Three types of carbonate stones (travertine, Lecce stone, and Carrara marble) characterized by different porosities were artificially stained with copper sulphates and treated with the different PVA-B-AG formulations. The effectiveness of the treatment was directly monitored on the stones using a multi-technique approach that included scanning electron microscopy with energy dispersive spectroscopy (SEM-EDS) and non-invasive portable nuclear magnetic resonance (NMR). Additionally, the rheological properties of the gels were investigated, and the Fourier transform infrared attenuated total reflection spectroscopy (FTIR ATR) was used to analyse the chemical structure of the gel before and after treatment, aiming to understand the changes induced by the cleaning process.