Previous synthesis routes created apatites in low crystallinity and high crystallinity states, but a wider range will extend the design capabilities of apatites for hard tissue replacements. While high crystallinity apatites are more conventional, this work investigated lower crystallinity variations from an amorphous state to low crystallinity apatite. Carbonated hydroxyapatite was prepared by precipitating an amorphous phase followed by crystallization at 650 °C at slow (5 °C min⁻¹) and fast heating rates (60 °C min⁻¹). The effect of processing conditions on crystallinity and structural changes was evaluated by thermal analysis, X-ray diffraction, transmission electron microscopy, Fourier transform infrared and Raman spectroscopy. Furthermore, peak deconvolution of IR and Raman spectra resolved the carbonate and phosphate bands and revealed the carbonate and crystalline phase content in CHAp. Similar to precipitation of crystalline apatites, the crystallization at elevated temperature led to carbonate in both the phosphate and hydroxyl positions. Heating at 650 °C provided a nanosized spherical hydroxyapatite containing carbonate controlled by the heating rate. This creates a mechanism for creating a large range in crystallinity with a greater resorption capability for regenerative medicine.

Bioactive calcium phosphate coatings were deposited by radio-frequency magnetron sputtering from biphasic targets of hydroxyapatite and tricalcium phosphate, sintered at different mass % ratios. According to Raman scattering and X-ray diffraction data, the deposited hydroxyapatite coatings have a disordered structure. High-temperature treatment of the coatings in air leads to a transformation of the quasi-amorphous structure into a crystalline one. A correlation has been observed between the increase in the Ca content in the coatings and a subsequent decrease in Ca in the biphasic targets after a series of deposition processes. It was proposed that the addition of tricalcium phosphate to the targets would led to a finer coating's surface topography with the average size of 78 nm for the structural elements.